PALDUR® R 15 GF 30 Datasheet,PBT,pal plast GmbH-SHANGHAI SUSHENG

Message
PALDUR®R 15 GF 30 is a polybutene terephthalate (PBT) product, which contains a 30% glass fiber reinforced material. It can be processed by injection molding and is available in Europe. PALDUR®R 15 GF 30 applications include electrical/electronic applications, wire and cable, and automotive industries. Features include: flame retardant/rated flame High stiffness high strength chemical resistance Wear-resistant

General Information
Filler / Reinforcement	Glass fiber reinforced material, 30% filler by weight
Features	Rigidity, high High strength Good chemical resistance Good wear resistance
Uses	Electrical/Electronic Applications Application in Automobile Field Communication Equipment
Forms	Particle
Processing Method	Injection molding

Physical	Nominal Value	Unit	Test Method
Density	1.54	g/cm³	ISO 1183
Water Absorption			ISO 62
Saturated, 23°C	0.38	%	ISO 62
Equilibrium, 23°C, 50% RH	14	%	ISO 62

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus (23°C)	9450	MPa	ISO 527-2/1A/1
Tensile Stress (Break, 23°C)	145	MPa	ISO 527-2/1A/5
Tensile Strain (Break, 23°C)	2.5	%	ISO 527-2/1A/5

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength (23°C)	9.5	kJ/m²	ISO 179/1eA
Charpy Unnotched Impact Strength (23°C)	58	kJ/m²	ISO 179/1eU

Thermal	Nominal Value	Unit	Test Method
Vicat Softening Temperature	214	°C	ISO 306/B50
Melting Temperature (DSC)	225	°C	ISO 3146

Electrical	Nominal Value	Unit	Test Method
Comparative Tracking Index (Solution A)	350	V	IEC 60112

Flammability	Nominal Value	Unit	Test Method
Flame Rating (1.60 mm)	HB		UL 94

Additional Information
Tensile Modulus, ISO 527, 23°C, 1 mm/min, Type A: 9000 to 9900 MPaTensile Stress at Break, ISO 527, 23°C, 5 mm/min, Type A: 140 to 150 MPaTensile Strain at Break, ISO 527, 23°C, 5 mm/min, Type A: 2 to 3 %Charpy Unnotched Impact, ISO 179, Type 1, Edgewise, 23°C: 50 to 65 kJ/m²Charpy Notched Impact, ISO 179, Type 1, Edgewise, Notch A, 23°C: 8 to 11 kJ/m²Vicat Softening Temperature, ISO 306, B50 (50°C/h 50N): 212 to 215 °CDensity, ISO 1183: 1.53 to 1.55 g/cm³Water Absorption, ISO 62, 23°C, Saturation: 0.35 to 0.4 %Moisture Absorption, ISO 62, 23°C, 50% RH: 0.12 to 0.15 %

Additional Information

Tensile Modulus, ISO 527, 23°C, 1 mm/min, Type A: 9000 to 9900 MPaTensile Stress at Break, ISO 527, 23°C, 5 mm/min, Type A: 140 to 150 MPaTensile Strain at Break, ISO 527, 23°C, 5 mm/min, Type A: 2 to 3 %Charpy Unnotched Impact, ISO 179, Type 1, Edgewise, 23°C: 50 to 65 kJ/m²Charpy Notched Impact, ISO 179, Type 1, Edgewise, Notch A, 23°C: 8 to 11 kJ/m²Vicat Softening Temperature, ISO 306, B50 (50°C/h 50N): 212 to 215 °CDensity, ISO 1183: 1.53 to 1.55 g/cm³Water Absorption, ISO 62, 23°C, Saturation: 0.35 to 0.4 %Moisture Absorption, ISO 62, 23°C, 50% RH: 0.12 to 0.15 %

Resin Grade	Manufacturer	Category	Trademark
RTP 1305 TFE 10	RTP Company	PPS	RTP
Bayblend® ET3036 FR	Covestro - Polycarbonates	PC+ABS	Bayblend®
Huafon HF-3795A	Huafon Group Co., Ltd.	TPU-Polyester	Huafon
ISPLEN® PB 180 A4M	REPSOL	PP Impact Copolymer	ISPLEN®
Karina STRAW PVC COMPOUND 828-38/ 98-AY-ERYB	Karina Ind. e Com. de Plásticos Ltda	PVC, Unspecified	Karina

Category:	PBT , Polybutylene Terephthalate
Manufacturer:	pal plast GmbH
Trademark:	PALDUR®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	bQquka_PALDUR-R-15-GF-30.pdf
PRICE:	Order Products email sales@su-jiao.com