Unigel PS U8884
| Category: | PS (HIPS) , High Impact Polystyrene |
| Manufacturer: | Unigel Plásticos |
| Trademark: | Unigel PS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bQAHnx_Unigel-PS-U8884.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.06 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 2.8 | g/10 min | ASTM D1238 |
| Water Absorption (Equilibrium) | 0.070 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1600 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 19.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | > 50 | % | ASTM D638 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.50 mm) | 110 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.30 mm) | 85.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 90.0 | °C | ASTM D1525 1 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SureSpec RP-800C | Genesis Polymers | PP Random Copolymer | SureSpec |
| Nypol® PA A3 G20 V10 PRTA010 NR302 MSP | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| Formolene® 6550A | Formosa Plastics Corporation, U.S.A. | PP Impact Copolymer | Formolene® |
| Iupilon® GPX2050DF | Mitsubishi Engineering-Plastics Corp | PC | Iupilon® |
| Polifor® 12 CA/40 H-D NATURALE Y1 | SO.F.TER. SPA | PP Homopolymer | Polifor® |