Chemlon® 66GS8H
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Teknor Apex Company (Chem Polymer) |
| Trademark: | Chemlon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bPtGWG_Chemlon-66GS8H.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 66GS8H is a 40% glass-sphere filled, heat stabilised injection moulding grade of nylon 66. It has lower differential shrinkage and warpage and so is often suitable for use in applications requiring greater dimensional accuracy. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.44 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | 0.90 - 1.5 | -- | % | Internal method |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 6300 | 3200 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 90.0 | 45.0 | MPa | ISO 527-2 |
| Flexural Modulus | 5000 | 2300 | MPa | ISO 178 |
| Flexural Stress 2 | 155 | 75.0 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 5.0 | 8.0 | kJ/m² | ISO 179 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | > 240 | 235 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 220 | 180 | °C | ISO 75-2/A |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+14 | 1.0E+11 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+16 | 1.0E+14 | ohms·cm | IEC 60093 |
| Dielectric Strength (3.00 mm) | 15 | 13 | kV/mm | IEC 60243-1 |
| Dissipation Factor (1 MHz) | 0.020 | 0.080 | IEC 60250 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | HB | -- | Internal method | |
| Glow Wire Flammability Index (1.50 mm) | 650 | -- | °C | IEC 60695-2-12 |
| Oxygen Index | 27 | -- | % | ISO 4589-2 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 100 | °C | |
| Drying Time | 2.0 | hr | |
| Rear Temperature | 270 - 290 | °C | |
| Middle Temperature | 270 - 290 | °C | |
| Front Temperature | 270 - 290 | °C | |
| Processing (Melt) Temp | < 300 | °C | |
| Mold Temperature | 60.0 - 80.0 | °C | |
| Injection Rate | Fast | ||
| Screw Speed | 50 - 200 | rpm |
| Injection instructions |
|---|
| 背压：低注射压力：高如果材料在空气中暴露的时间不超过3小时，则无需干燥。 |
| Note Message | |
|---|---|
| 1 . | Mould shrinkage is significantly influenced by many factors including wall thickness, gating, component shape and moulding conditions.The range values stated were determined from specimen bar mouldings of 1.5mm to 4mm wall thickness. They are provided as a guide for comparison purposes only and no guarantee should be inferred from their inclusion. (Specimens measured in the dry state, 24 hours after moulding). |
| 2 . | Break |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Bapolene® 80 | Bamberger Polymers, Inc. | PET | Bapolene® |
| Fainplast PVC PH 50/AM-UV | Fainplast Compounds S.r.l | PVC, Flexible | Fainplast PVC |
| POLIMAXX HI830 | IRPC Public Company Limited | PS (HIPS) | POLIMAXX |
| POLYFLAM® RIPP 2000 | A. Schulman Europe | PP Copolymer | POLYFLAM® |
| KMI PP KM-053JB | KMI Group, Inc. | PP Impact Copolymer | KMI PP |