Eleme BFG00919
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Eleme Petrochemical Company Ltd |
| Trademark: | Eleme |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bPGiDo_Eleme-BFG00919.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| No slip. Stretch wrap, lamination, co-extrusion, etc |
| General Information | |
|---|---|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.919 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.90 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| Secant Modulus | ASTM D882 | ||
| MD : 25 µm | 220 | MPa | |
| TD : 25 µm | 276 | MPa | |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 25 µm | 11.0 | MPa | |
| TD : Yield, 25 µm | 11.0 | MPa | |
| MD : Break, 25 µm | 53.0 | MPa | |
| TD : Break, 25 µm | 35.0 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 25 µm | 350 | % | |
| TD : Break, 25 µm | 850 | % | |
| Dart Drop Impact 1(25 µm) | 3.2 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 25 µm | 1.2 | g | |
| TD : 25 µm | 26 | g |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 98.0 | °C | ASTM D1525 2 |
| Note Message | |
|---|---|
| 1 . | F50, 3.8 cm dart, 66 cm drop height |
| 2 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 8200-70 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| VITAMIDE® AR86BK6273 | Jackdaw Polymers | Nylon 66 | VITAMIDE® |
| Bapolene® 213B | Bamberger Polymers, Inc. | LDPE | Bapolene® |
| Ducor® 2300 K | Ducor Petrochemicals BV | PP Impact Copolymer | Ducor® |
| LUBAN™ 1102 K | Oman Oil Refineries & Petroleum Indistries Co. (Orpic) | PP Homopolymer | LUBAN™ |