| LEXAN resin 3413R is a flame retardant polycarbonate grade with 30% glass fiber reinforcement to meet UL 94 V1 listing at 1.5mm. This grade can be considered for applications requiring higher stiffness and flame retardancy. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | ASTM D792 | ||
| -- | 1.43 | g/cm³ | ASTM D792 |
| -- | 1.44 | g/cm³ | ASTM D792 |
| Specific Volume | 0.697 | cm³/g | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/5.0 kg) | 19 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.10 - 0.30 | % | Internal method |
| Water Absorption | ASTM D570 | ||
| 24 hr | 0.14 | % | ASTM D570 |
| Equilibrium, 23°C | 0.26 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ASTM D785 | ||
| Class m | 92 | ASTM D785 | |
| Class r | 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Break) | 100 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 2.0 | % | ASTM D638 |
| Flexural Modulus 3(50.0 mm Span) | 6620 | MPa | ASTM D790 |
| Flexural Strength 4(Yield, 50.0 mm Span) | 153 | MPa | ASTM D790 |
| Taber Abrasion Resistance (1000 Cycles, 1000 g, CS-17 Wheel) | 24.0 | mg | ASTM D1044 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 110 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 1100 | J/m | ASTM D4812 |
| Dart Drop Impact (23°C) | 5.42 | J | ASTM D3029 |
| Tensile Impact Strength 5 | 67.2 | kJ/m² | ASTM D1822 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.40mm | 152 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.40mm | 146 | °C | ASTM D648 |
| Vicat Softening Temperature | 166 | °C | ASTM D1525 6 |
| CLTE - Flow (-40 to 95°C) | 2.2E-5 | cm/cm/°C | ASTM E831 |
| Specific Heat | 1130 | J/kg/°C | ASTM C351 |
| Thermal Conductivity | 0.22 | W/m/K | ASTM C177 |
| RTI Elec | 120 | °C | UL 746 |
| RTI Imp | 120 | °C | UL 746 |
| RTI | 130 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+17 | ohms·cm | ASTM D257 |
| Dielectric Strength (3.20 mm, in Air) | 19 | kV/mm | ASTM D149 |
| Dielectric Constant | ASTM D150 | ||
| 50 Hz | 3.35 | ASTM D150 | |
| 60 Hz | 3.35 | ASTM D150 | |
| 1 MHz | 3.31 | ASTM D150 | |
| Dissipation Factor | ASTM D150 | ||
| 50 Hz | 1.1E-3 | ASTM D150 | |
| 60 Hz | 1.1E-3 | ASTM D150 | |
| 1 MHz | 7.0E-3 | ASTM D150 | |
| Arc Resistance 7 | PLC 7 | ASTM D495 | |
| Comparative Tracking Index (CTI) | PLC 5 | UL 746 | |
| High Amp Arc Ignition (HAI) | PLC 4 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) | PLC 3 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 0 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.47 mm | V-1 | UL 94 | |
| 3.00 mm | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Drying Time, Maximum | 48 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 - 60 | % | |
| Rear Temperature | 293 - 316 | °C | |
| Middle Temperature | 304 - 327 | °C | |
| Front Temperature | 316 - 338 | °C | |
| Nozzle Temperature | 310 - 332 | °C | |
| Processing (Melt) Temp | 316 - 338 | °C | |
| Mold Temperature | 82.2 - 116 | °C | |
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 40 - 70 | rpm | |
| Vent Depth | 0.025 - 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | Type 1, 5.0 mm/min |
| 2 . | Type 1, 5.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | Type S |
| 6 . | 标准 B (120°C/h), 载荷2 (50N) |
| 7 . | Tungsten electrode |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rilsan® BESVOA MED | Arkema | Nylon 11 | Rilsan® |
| Shin-Etsu RTV KE-1843 | Shin-Etsu Silicones of America | Silicone Rubber, RTV-1 | Shin-Etsu RTV |
| SILVER® EUL105-K/UL1007 | Guangdong Silver Age Sci & Tech. Co., Ltd | PVC, Unspecified | SILVER® |
| AKROMID® B3 GF 10 natural (2829) | AKRO-PLASTIC GmbH | Nylon 6 | AKROMID® |
| Hostacom MT8220 | LyondellBasell Industries | PP Copolymer | Hostacom |