Key Features:
Colors:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.22 - 1.28 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 13 - 19 | g/10 min | ASTM D1238 |
| Carbon Black Content 1 | 0.80 - 1.2 | % | ASTM D1603 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 23°C) | > 24.0 | MPa | ASTM D638 |
| Flexural Modulus - Tangent (23°C) | > 2240 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | > 40 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | > 110 | °C | ASTM D648 |
| 1.8 MPa, not annealed | > 78.9 | °C | ASTM D648 |
| Thermal stability- 1000 hours (150°C) | Pass | Internal method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 - 93.3 | °C | |
| Drying Time | 0.0 - 8.0 | hr | |
| Rear Temperature | 193 - 238 | °C | |
| Middle Temperature | 193 - 238 | °C | |
| Front Temperature | 193 - 238 | °C | |
| Nozzle Temperature | 193 - 238 | °C | |
| Mold Temperature | 26.7 - 60.0 | °C | |
| Back Pressure | 0.00 - 0.689 | MPa | |
| Screw Speed | 50 - 150 | rpm |
| Injection instructions |
|---|
| Hot Runner Temperature (if applicable): 420 to 450°F |
| Note Message | |
|---|---|
| 1 . | PP-5344-9000 only |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sanren M3500CA (1st-grade) | SINOPEC Shanghai Petrochemical Co. Ltd. | PP Homopolymer | Sanren |
| Nivionplast® B C306MB NERO900 | SO.F.TER. SPA | Nylon 6 | Nivionplast® B |
| HAIPLEN EP50 T6 | Taro Plast S.p.A. | PP Copolymer | HAIPLEN |
| Hanwha Total PP BJ732 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP Impact Copolymer | Hanwha Total PP |
| LNP™ STAT-KON™ RE006 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ STAT-KON™ |