Edgetek™ PC-000/000 BK710
| Category: | PC , Polycarbonate |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Edgetek™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bOe9bo_Edgetek-PC-000-000-BK710.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Un-Filled Polycarbonate Resin with Black Color |
| General Information | |
|---|---|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Molding Shrinkage (3.00 mm) | 0.50 - 0.70 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 55.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | > 50 | % | ASTM D638 |
| Flexural Modulus 3 | 2400 | MPa | ASTM D790 |
| Flexural Strength 4 | 90.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 500 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 125 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+12 | ohms | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 - 130 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Processing (Melt) Temp | 280 - 310 | °C | |
| Mold Temperature | 80.0 - 120 | °C |
| Injection instructions |
|---|
| Injection Pressure: MED-HIGHHold Pressure: MED-HIGHScrew Speed: MODERATEBack Pressure: LOW |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Nylfor® A2 GB/30 FR2/3A UV BLACK | SO.F.TER. SPA | Nylon 66 | Nylfor® |
| Hyundai EP PA6 LS405 | HYUNDAI EP Co., Ltd. | Nylon 6 | Hyundai EP PA6 |
| Lupolen 5261 Z Q 456 B | LyondellBasell Industries | HDPE | Lupolen |
| PHOENIX™ 5152 | Phon Tech Industrial Company | SBC | PHOENIX™ |
| Plenco 04349 (Compression) | Plastics Engineering Co. | Phenolic | Plenco |