ColorFast® JCT1000
| Category: | PC+ABS+SMA , Polycarbonate + ABS + SMA |
| Manufacturer: | LTL Color Compounders, Inc. |
| Trademark: | ColorFast® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bOGnZz_ColorFast-JCT1000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Unique PC/ABS/SMA alloy with improved processing and reduced plate-out |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.19 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (260°C/2.16 kg) | 14 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.18 mm) | 0.40 to 0.60 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 122 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | ASTM D638 | ||
| Yield | 60.0 | MPa | |
| Break | 55.8 | MPa | |
| Tensile Elongation 2 | ASTM D638 | ||
| Yield | 4.0 | % | |
| Break | 90 | % | |
| Flexural Modulus 3 | 2700 | MPa | ASTM D790 |
| Flexural Strength 4 | 95.1 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 640 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.35 mm) | 95.0 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Shot Size | 30 to 60 | % | |
| Rear Temperature | 210 to 254 | °C | |
| Middle Temperature | 216 to 260 | °C | |
| Front Temperature | 227 to 274 | °C | |
| Nozzle Temperature | 232 to 274 | °C | |
| Processing (Melt) Temp | 232 to 274 | °C | |
| Mold Temperature | 60.0 to 82.2 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 30 to 75 | rpm | |
| Vent Depth | 0.038 to 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | 51 mm/min |
| 2 . | 51 mm/min |
| 3 . | 51 mm/min |
| 4 . | 51 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| THERMOLAST® K TC7FRN (Series: FR) | KRAIBURG TPE | TPE | THERMOLAST® K |
| TPV Elastoprene® N55A-E | ELASTORSA Elastomeros Riojanos S.A. | PP+EPDM | TPV Elastoprene® |
| GPPC ABS D-120 | GPPC Chemical Co., Ltd. | ABS | GPPC ABS |
| HANWHA KL-701 | Hanwha Chemical | PVC, Unspecified | HANWHA |
| SABIC® PPcompound 9310 | Saudi Basic Industries Corporation (SABIC) | PP, Unspecified | SABIC® PPcompound |