MXSTEN® CV77523
| Category: | Plastomer , Ethylene-based Plastomer |
| Manufacturer: | Westlake Chemical Corporation |
| Trademark: | MXSTEN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bO8GPM_MXSTEN-CV77523.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
MXSTEN® CV77523 is a polyethylene plastomer designed for blown film extrusion that contains high slip, very high antiblock and polymer processing aid additives. Films produced with this resin exhibit very good strength properties, and low seal initiation temperatures. Application/Uses: Agricultural tubing Blown film Food packaging |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.906 | g/cm³ | ASTM D4883 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.50 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| secant modulus 1 | ASTM D882 | ||
| 1% secant, MD : 25 µm, blown film | 124 | MPa | ASTM D882 |
| 1% secant, TD : 25 µm, blown film | 145 | MPa | ASTM D882 |
| Tensile Strength 2 | ASTM D882 | ||
| TD : Yield, 25 µm, blown film | 7.58 | MPa | ASTM D882 |
| MD : Broken, 25 µm, blown film | 55.2 | MPa | ASTM D882 |
| TD : Broken, 25 µm, blown film | 51.7 | MPa | ASTM D882 |
| Tensile Elongation 3 | ASTM D882 | ||
| MD : Broken, 25 µm, blown film | 600 | % | ASTM D882 |
| TD : Broken, 25 µm, blown film | 1000 | % | ASTM D882 |
| Dart Drop Impact 4(25 µm, Blown Film) | 1200 | g | ASTM D1709 |
| Elmendorf Tear Strength 5 | ASTM D1922 | ||
| MD : 25 µm, blown film | 450 | g | ASTM D1922 |
| TD : 25 µm, blown film | 650 | g | ASTM D1922 |
| Seal Initiation Temperature 6(25 µm, Blown Film) | 82.0 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 25.4 µm, Blown Film) | 35 | ASTM D2457 | |
| Haze (25.4 µm, Blown Film) | 30 | % | ASTM D1003 |
| Additional Information |
|---|
| Extrusion conditions used to produce 1 mil (0.025 mm) film include a 6" die, 2.5":24:1 L:D barrier screw, 2.4:1 BUR, 100-mil die gap, 15" frostline height, 450° F melt temperature, and 7.5 lb/hr/inch die output. Density results are on Base Resin. |
| Note Message | |
|---|---|
| 1 . | Test run at 23°C (73°F) and 50% relative humidity |
| 2 . | Test run at 23°C (73°F) and 50% relative humidity |
| 3 . | Test run at 23°C (73°F) and 50% relative humidity |
| 4 . | Test run at 23°C (73°F) and 50% relative humidity |
| 5 . | Test run at 23°C (73°F) and 50% relative humidity |
| 6 . | Seal initiation temperature is the temperature at which 200 g/inch seal strength is achieved. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SAXALEN™ PPC339T20 | SAX Polymers | PP Copolymer | SAXALEN™ |
| Moplen HP562T | PolyMirae | PP Homopolymer | Moplen |
| Trilene® BI9.0GA | Chandra Asri Petrochemical | PP Impact Copolymer | Trilene® |
| NOVAREX® 7020R | Mitsubishi Engineering-Plastics Corp | PC | NOVAREX® |
| Hostacom PPU X9067HS C12507 | LyondellBasell Industries | PP Copolymer | Hostacom |