Lupolen 4552D black Datasheet,HDPE,LyondellBasell Industries-SHANGHAI SUSHENG

Lupolen 4552D black

Category:	HDPE , High Density Polyethylene
Manufacturer:	LyondellBasell Industries
Trademark:	Lupolen
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	bO2x2E_Lupolen-4552D-black.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
Lupolen 4552D black is a UV and thermal stabilised high-density polyethylene with a multi-modal molecular weight distribution designed for extrusion. Lupolen 4552D black is produced with the advanced Hostalen technology which provides the material with excellent mechanical and physical properties. The excellent dispersion of the fine particle sized carbon black ensures the material has excellent weathering resistance. Lupolen 4552D black fulfils the requirements of DIN 30670, NFA 49710, CAN, CSA-Z245.21-M98 and prEN 10285 when used in combination with the maleic-anhydrided grafted adhesives Lucalen G3710E P and a compatible fusion-bonded epoxy powder. Lupolen 4552D black is recommended as the topcoat layer in 3LPE pipe coating applications and is suitable for severe laying conditions even at elevated temperatures. Lupolen 4552D black can be used up to 85°C service temperature of the pipeline when used in combination with the maleic-anhydride grafted adhesives Lucalen G3710E or Lucalen G3710E P and a compatible fusion-bonded epoxy powder. This grade is available in black, in pellet form.

Message

Lupolen 4552D black is a UV and thermal stabilised high-density polyethylene with a multi-modal molecular weight distribution designed for extrusion. Lupolen 4552D black is produced with the advanced Hostalen technology which provides the material with excellent mechanical and physical properties. The excellent dispersion of the fine particle sized carbon black ensures the material has excellent weathering resistance.

Lupolen 4552D black fulfils the requirements of DIN 30670, NFA 49710, CAN, CSA-Z245.21-M98 and prEN 10285 when used in combination with the maleic-anhydrided grafted adhesives Lucalen G3710E P and a compatible fusion-bonded epoxy powder.

Lupolen 4552D black is recommended as the topcoat layer in 3LPE pipe coating applications and is suitable for severe laying conditions even at elevated temperatures. Lupolen 4552D black can be used up to 85°C service temperature of the pipeline when used in combination with the maleic-anhydride grafted adhesives Lucalen G3710E or Lucalen G3710E P and a compatible fusion-bonded epoxy powder.

This grade is available in black, in pellet form.

General Information
Additive	Carbon Black (2%) Heat Stabilizer UV Stabilizer
Features	Bacteria Resistant Bimodal Molecular Weight Distribution Fungus Resistant Good Chemical Resistance Good Creep Resistance Good Impact Resistance Good UV Resistance Good Weather Resistance Heat Stabilized High ESCR (Stress Crack Resist.) Low to No Water Absorption Ozone Resistant
Uses	Coating Applications Pipe Coatings
Agency Ratings	CSA Z245.21-M98 DIN 30670 NF A 49-710 prEN 10285
Appearance	Black
Forms	Pellets
Processing Method	Extrusion Extrusion Coating

Physical	Nominal Value	Unit	Test Method
Density			ISO 1183
-- ¹	> 0.930	g/cm³
-- ²	0.956	g/cm³
Apparent Density	> 0.50	g/cm³	ISO 60
Melt Mass-Flow Rate (MFR)			ISO 1133
190°C/2.16 kg	0.42	g/10 min
190°C/5.0 kg	1.7	g/10 min
Environmental Stress-Cracking Resistance (F0)	> 2000	hr	ASTM D1693
Carbon Black Content	2.2	%	ISO 6964
Moisture Content	0.035	%	ISO 15512

Thermal	Nominal Value	Unit	Test Method
Oxidation Induction Time			ISO 11357-6
200°C	> 30	min
210°C	> 30	min
220°C	> 20	min

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore D)	60		ASTM D2240, ISO 868

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus (23°C)	900	MPa	ISO 527-2/1
Tensile Stress (Yield, 23°C)	23.0	MPa	ISO 527-2/50
Tensile Elongation (Break)	700	%	ASTM D638

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact Strength (-20°C)	> 3.0	kJ/m²	ISO 180

Thermal	Nominal Value	Unit	Test Method
Brittleness Temperature	< -70.0	°C	ASTM D746
Vicat Softening Temperature	124	°C	ISO 306/A50
Melting Temperature (DSC)	130	°C	ISO 3146

Electrical	Nominal Value	Unit	Test Method
Volume Resistivity	1.0E+17	ohms·cm	ASTM D257, IEC 60093

Extrusion	Nominal Value	Unit
Melt Temperature	190 to 260	°C

Note Message
1 .	Base Polymer
2 .	Compound

Resin Grade	Manufacturer	Category	Trademark
RTP 683 HEC	RTP Company	ABS	RTP
Rhelon F1530H-01	RheTech, Inc.	Nylon 6	Rhelon
Hostalen GC 7260 LS	LyondellBasell Industries	HDPE	Hostalen
KumhoSunny PBT/ASA HBA5810M	Shanghai KumhoSunny Plastics Co., Ltd.	PBT+ASA	KumhoSunny PBT/ASA
MAXATEL® AC109UV-BK	Pier One Polymers, Inc.	Acetal (POM) Copolymer	MAXATEL®

Resin Grade

Manufacturer