EL-Lene™ M9001RW
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | SCG Chemicals Co., Ltd. |
| Trademark: | EL-Lene™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bMxV1U_EL-Lene-M9001RW.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| M9001RW and Marvel M90 are linear-low density polyethylene (LLDPE) for rotational molding applications. M9001RW is a natural color available in powder and pellet form. With excellent stiffness good impact strength and toughness. Both of them are suitable for rotational molding of large water tanks and other general rotational molded articles. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.939 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 3.2 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 60 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | ASTM D638 | ||
| Yield | 21.0 | MPa | ASTM D638 |
| Fracture | 28.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 1100 | % | ASTM D638 |
| Bending modulus- Transverse flow 3 | 750 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| ARM Impact 4(-40°C) | 122 | J | ARM |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Crystallization Point | 113 | °C | ASTM D2117 |
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 75.0 | °C | ASTM D648 |
| Brittleness Temperature | < -60.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 122 | °C | ASTM D1525 |
| Melting Temperature | 127 | °C | ASTM D2117 |
| Additional Information |
|---|
| UV Resistance Level, ASTM D2565: 8Oven Temperature: 250 to 300°C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 5 mm rotomolded sample |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2800B-60A HF | RTP Company | TPV | RTP |
| Xuchuan XWB-3330 | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| Alkatuff® 425 | Qenos Pty Ltd | LLDPE | Alkatuff® |
| LEXAN™ IR2840 resin | SABIC Innovative Plastics | PC | LEXAN™ |
| 3M™ Dyneon™ Fluoroelastomer FPO 3520 | 3M Advanced Materials Division | Fluorelastomer | 3M™ Dyneon™ Fluoroelastomer |