Durethan® BKV 130 H3.0 DUS008 000000
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | LANXESS GmbH |
| Trademark: | Durethan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bMw8Fd_DurethanBKV130H30DUS008000000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA 6, 30 % glass fibers, injection molding, improved impact strength, heat-aging stabilized |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.37 | -- | g/cm³ | ISO 1183 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 9000 | 5200 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 160 | 100 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 4.0 | 7.0 | % | ISO 527-2/5 |
| Flexural Modulus 1(23°C) | 8000 | 4800 | MPa | ISO 178/A |
| Flexural Stress 2 | ||||
| 3.5% strain | 230 | 115 | MPa | ISO 178/A |
| 23°C | 250 | 145 | MPa | ISO 178 |
| Flexural Strain at Flexural Strength 3(23°C) | 5.0 | 7.0 | % |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Shortname | PA6-HI, GHR, 14-090, GF30 | -- | ISO 1874 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Residual Moisture Content | 0.030 - 0.12 | % | Karl Fisher |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 10 | 10 | kJ/m² | ISO 179/1eA |
| 23°C | 18 | 28 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 80 | 80 | kJ/m² | ISO 179/1eU |
| 23°C | 95 | 110 | kJ/m² | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 220 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 205 | -- | °C | ISO 75-2/A |
| Melting Temperature 4 | 222 | -- | °C | ISO 11357-3 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Dry Air Dryer | 80.0 | °C | |
| Drying Time - Dry Air Dryer | 2.0 - 6.0 | hr | |
| Processing (Melt) Temp | 260 - 290 | °C | |
| Mold Temperature | 80.0 - 100 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | Pull Rate: 2 mm/min; 50% RH |
| 4 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Nylene® 9643 | Custom Resins Group | Nylon 66/6 | Nylene® |
| ELASTOSIL® LR 3162 A/B | Wacker Chemie AG | Silicone | ELASTOSIL® LR |
| InvisiSil™ IVS4752 | Momentive Performance Materials Inc. | Silicone | InvisiSil™ |
| TechnoElast V A6000 I 2 sw | TechnoCompound GmbH | TPE | TechnoElast |
| ESTOPLAST SR 1500GY04 | Ester Industries Ltd. | ABS | ESTOPLAST SR |