Lupol® GP3156F
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | Lupol® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bMbvOC_Lupol-GP3156F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LUPOL GP-3156F is designed for injection molding of large parts by reinforced with mineral filler, This product features excellent dimensional stability and low warpage characteristics, thus ideal for interior materials of automobiles,and electric/electronic parts. Applications: Automobile interior, electric/electronic components. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.32 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 6.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.90 - 1.3 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm) | 27.5 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 20 | % | ASTM D638 |
| Flexural Modulus 3(6.40 mm) | 1770 | MPa | ASTM D790 |
| Flexural Strength 4(6.40 mm) | 38.2 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 49 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed, 3.20 mm) | 135 | °C | ASTM D648 |
| RTI Elec | 125 | °C | UL 746 |
| RTI Imp | 120 | °C | UL 746 |
| RTI | 120 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.794 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 - 80.0 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Minimum Moisture Content | > 0.010 | % | |
| Rear Temperature | 190 - 210 | °C | |
| Middle Temperature | 200 - 230 | °C | |
| Front Temperature | 200 - 230 | °C | |
| Nozzle Temperature | 210 - 230 | °C | |
| Processing (Melt) Temp | 200 - 230 | °C | |
| Mold Temperature | 40.0 - 60.0 | °C | |
| Back Pressure | 29.4 - 58.8 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Injection instructions |
|---|
| First injection pressure: 30 to 120 kg/cm²Second injection pressure: 20 to 100 kg/cm² |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 10 mm/min |
| 4 . | 10 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 5199-80 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| XENOY™ HX6600HP resin | SABIC Innovative Plastics Asia Pacific | PC+PBT | XENOY™ |
| Cheng Yu FV30G15 | Cheng Yu Plastic Company Limited | Acetal (POM) Homopolymer | Cheng Yu |
| Expandable PS F11MB-n | INEOS Styrenics International SA | PS (EPS) | Expandable PS |
| Hyundai EP PPF HG380 | HYUNDAI EP Co., Ltd. | PP Homopolymer | Hyundai EP PPF |