Durethan® BKV 30 H2.0 000000
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | LANXESS GmbH |
| Trademark: | Durethan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bLim5z_DurethanBKV30H20000000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA 6, 30 % glass fibers, injection molding, heat-aging stabilized |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | ||||
| -- | 1.36 1.36 | -- | g/cm³ | ASTM D792 |
| 23°C | 1.38 | -- | g/cm³ | ISO 1183 |
| Apparent Density | 0.70 | -- | g/cm³ | ISO 60 |
| Water Absorption | ISO 62 | |||
| Saturated, 23°C | 7.0 | -- | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 2.1 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | ||||
| 23°C 1 | 9200 | 5600 | MPa | ASTM D638 |
| 23°C | 9600 | 5900 | MPa | ISO 527-2/1 |
| Tensile Strength | ||||
| Fracture, 23°C | 180 | 100 | MPa | ASTM D638 |
| Fracture, 23°C | 170 | 100 | MPa | ISO 527-2/5 |
| Tensile Elongation | ||||
| Fracture, 23°C | 3.0 | 6.0 | % | ASTM D638 |
| Fracture, 23°C | 3.5 | 6.5 | % | ISO 527-2/5 |
| Tensile Creep Modulus (1000 hr) | -- | 4100 | MPa | ISO 899-1 |
| Flexural Modulus | ||||
| 23°C | 8300 | 5000 | MPa | ASTM D790 |
| 23°C 2 | 8500 | 5100 | MPa | ISO 178/A |
| Flexural Strength | ||||
| 23°C | 280 | 170 | MPa | ASTM D790 |
| 3.5% strain, 23°C | 265 | 140 | MPa | ISO 178/A |
| 23°C 3 | 280 | 170 | MPa | ISO 178/A |
| Flexural Strain at Flexural Strength 4(23°C) | 4.0 | 6.0 | % | ISO 178/A |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Behavior 5(> 1.00 mm) | passed | -- | ISO 3795 |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Shortname | PA 6, MHR, 14-100, GF30 | -- | ISO 1874 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Residual Moisture Content | 0.030 - 0.12 | % | Karl Fisher |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 10 | 10 | kJ/m² | ISO 179/1eA |
| 23°C | 15 | 20 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 70 | 70 | kJ/m² | ISO 179/1eU |
| 23°C | 80 | 95 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | ||||
| -40°C, 3.18 mm | 100 | 100 | J/m | ASTM D256 |
| 23°C, 3.18 mm | 120 | 150 | J/m | ASTM D256 |
| -30°C | < 10 | < 10 | kJ/m² | ISO 180/1A |
| 23°C | 15 | 20 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | ISO 180/1U | |||
| -30°C | 65 | 65 | kJ/m² | ISO 180/1U |
| 23°C | 75 | 80 | kJ/m² | ISO 180/1U |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ||||
| 0.45 MPa, unannealed, 39.9mm | 215 | -- | °C | ASTM D648 |
| 0.45 MPa, not annealed | 215 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 200 | -- | °C | ISO 75-2/A |
| 1.8 MPa, annealing, 3.99mm | 200 | -- | °C | ASTM D648 |
| 8.0 MPa, not annealed | 110 | -- | °C | ISO 75-2/C |
| Vicat Softening Temperature | > 200 | -- | °C | ISO 306/B50, ISO 306/B120 |
| Melting Temperature 6 | 222 | -- | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | |||
| Flow : 23 to 55°C | 2.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 55°C | 8.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| RTI Elec | UL 746 | |||
| 0.830 mm | 120 | -- | °C | UL 746 |
| 1.50 mm | 120 | -- | °C | UL 746 |
| RTI Imp | UL 746 | |||
| 0.830 mm | 90.0 | -- | °C | UL 746 |
| 1.50 mm | 95.0 | -- | °C | UL 746 |
| RTI | UL 746 | |||
| 0.830 mm | 130 | -- | °C | UL 746 |
| 1.50 mm | 130 | -- | °C | UL 746 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+14 | 1.0E+12 | ohms | IEC 60093 |
| Volume Resistivity (23°C) | 1.0E+15 | 1.0E+12 | ohms·cm | IEC 60093 |
| Dielectric Strength (23°C, 3.00 mm) | 40 | 35 | kV/mm | IEC 60243-1 |
| Dielectric Constant 7 | IEC 60250 | |||
| 23°C, 50 Hz | 4.00 | 15.0 | IEC 60250 | |
| 23°C, 1 MHz | 4.00 | 5.00 | IEC 60250 | |
| Dissipation Factor | IEC 60250 | |||
| 23°C, 50 Hz | 5.0E-3 | 0.50 | IEC 60250 | |
| 23°C, 1 MHz | 0.015 | 0.16 | IEC 60250 | |
| Arc Resistance 8 | -- | 76.0 | sec | ASTM D495 |
| Comparative Tracking Index | -- | 400 | V | ASTM D3638 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.830 mm | HB | -- | UL 94 | |
| 1.50 mm | HB | -- | UL 94 | |
| 1.60 mm | HB | -- | UL 94 | |
| 3.00 mm | HB | -- | UL 94 | |
| 3.20 mm | HB | -- | UL 94 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Dry Air Dryer | 80.0 | °C | |
| Drying Time - Dry Air Dryer | 2.0 - 6.0 | hr | |
| Processing (Melt) Temp | 270 - 290 | °C | |
| Mold Temperature | 80.0 - 120 | °C |
| Note Message | |
|---|---|
| 1 . | 1.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 2 mm/min |
| 5 . | US-FMVSS302 |
| 6 . | 10°C/min |
| 7 . | Tinfoil Electrodes |
| 8 . | Tungsten Electrodes |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RELENE® 52GB010 | Reliance Industries Limited | HDPE | RELENE® |
| Sindustris ABS LLG850W | Sincerity Australia Pty Ltd. | ABS | Sindustris ABS |
| Staramide BST01 | Eurostar Engineering Plastics | Nylon 6 | Staramide |
| Vyncolit® FS-10-V0-P | Vyncolit N.V. | DAP | Vyncolit® |
| Alkathene® WRM124 | Qenos Pty Ltd | LLDPE | Alkathene® |