TAISOX 7350F
| Category: | EVA , Ethylene Vinyl Acetate Copolymer |
| Manufacturer: | Formosa Plastics Corporation |
| Trademark: | TAISOX |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bLfyI6_TAISOX-7350F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TAISOX 7350F is an ethylene vinyl acetate copolymer (EVA) material,. This product is available in North America, Europe or Asia Pacific,. The main features of TAISOX 7350F are:
Typical application areas include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.938 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.8 | g/10 min | ASTM D1238 |
| Vinyl Acetate Content | 18.0 | wt% |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 38 88 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield | 4.41 | MPa | ASTM D638 |
| Fracture | 14.7 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 800 | % | ASTM D638 |
| Flexural Modulus | 39.2 | MPa | ASTM D790 |
| Coefficient of Friction (Blown Film) | 0.50 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 30 | µm | |
| Film Thickness - Recommended / Available | 1.2-5.9 mil (30-150 µ) | ||
| secant modulus | ASTM D882 | ||
| 1% secant, MD : 30 µm, blown film | 34.3 | MPa | ASTM D882 |
| 1% secant, TD : 30 µm, blown film | 37.3 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 30 µm, blown film | 3.92 | MPa | ASTM D882 |
| TD : Yield, 30 µm, blown film | 2.94 | MPa | ASTM D882 |
| MD : Broken, 30 µm, blown film | 27.5 | MPa | ASTM D882 |
| TD : Broken, 30 µm, blown film | 24.5 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 30 µm, blown film | 500 | % | ASTM D882 |
| TD : Broken, 30 µm, blown film | 600 | % | ASTM D882 |
| Dart Drop Impact (30 µm, Blown Film) | 650 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 30 µm, blown film | 12 | g | ASTM D1922 |
| TD : 30 µm, blown film | 29 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -70.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 60.0 | °C | ASTM D1525 |
| Melting Temperature | 84.0 | °C |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 30.0 µm, Blown Film) | 90 | ASTM D2457 | |
| Haze (30.0 µm, Blown Film) | 3.0 | % | ASTM D1003 |
| Additional Information |
|---|
| Film extrusion preparation parameters: Screw: 60 mm L/D: 30 Blow up ratio: 2.5 Temperature160 to 200°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tarflen® SM-S25 | Grupa Azoty S.A. | PTFE | Tarflen® |
| Hostalen ACP 5831 D | LyondellBasell Industries | HDPE | Hostalen |
| ICORENE® N1012 | ICO Polymers EMEA, A Division of A. Schulman | EVA | ICORENE® |
| TECHNYL® A 60G1 V30 BLACK 61 | Solvay Engineering Plastics | Nylon 66 | TECHNYL® |
| Delas 190 | Shanghai Lin Gen Rubber Materials Co., Ltd. | PVC+NBR | Delas |