POLYPRO® 5014L(2)
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | YUHWA Korea Petrochemical Ind. Co., Ltd. |
| Trademark: | POLYPRO® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bLG18q_POLYPRO-5014L-2-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
POLYPRO® 5014L(2) is a Polypropylene Homopolymer (PP Homopolymer) material. It is available in Asia Pacific for blown film, cast film, or coextruded film. Primary attribute of POLYPRO® 5014L(2): Homopolymer. Typical applications include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.900 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 2.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 1.0 to 2.0 | % | Internal Method |
| Water Absorption (Equilibrium) | < 0.010 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 96 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 35.3 | MPa | ASTM D638 |
| Tensile Elongation (Break) | > 500 | % | ASTM D638 |
| Flexural Modulus | 1570 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 39 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 105 | °C | ASTM D648 |
| Vicat Softening Temperature | 152 | °C | ASTM D1525 |
| Peak Melting Temperature | 162 | °C | ASTM D3418 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| BCC Resins BC 8635E | BCC Products Inc. | TSU | BCC Resins |
| CPI PP 40 Black | CPI Binani, Inc. | PP, Unspecified | CPI PP |
| Ebalta AH 140 / LI 60 | Ebalta Kunststoff GmbH | Epoxy | Ebalta |
| LNP™ THERMOCOMP™ RF006H compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |
| Petrothene® LT573501 | LyondellBasell Industries | HDPE | Petrothene® |