Chemlon® 830GHI
| Category: | Nylon 6/12 , Polyamide 6/12 Copolymer |
| Manufacturer: | Teknor Apex Company (Chem Polymer) |
| Trademark: | Chemlon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bKYeOG_Chemlon-830GHI.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 830GHI is an impact modified, 30% glass fibre reinforced, heat stabilised grade of PA612. It offers good mechanical strength and low moisture absorption. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.27 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | 1.0 - 1.2 | % | Internal method |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.80 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | 133 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 4.0 | % | ISO 527-2 |
| Flexural Modulus | 6750 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 15 | kJ/m² | ISO 180/A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 175 | °C | ISO 75-2/A |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Rear Temperature | 240 - 280 | °C | |
| Middle Temperature | 240 - 280 | °C | |
| Front Temperature | 240 - 280 | °C | |
| Processing (Melt) Temp | 240 - 280 | °C | |
| Mold Temperature | 80.0 - 90.0 | °C | |
| Injection Rate | Fast | ||
| Back Pressure | Low | ||
| Screw Speed | Moderate |
| Injection instructions |
|---|
| No drying is necessary unless the material has been exposed to air for longer than three hours. The appearance of splash marks on the surface of mouldings indicates excessive moisture is present. |
| Note Message | |
|---|---|
| 1 . | Mould shrinkage is significantly influenced by many factors including wall thickness, gating, moulding shape and processing conditions. The range values given are determined from specimen bar mouldings of 1.5mm to 4mm wall thickness. They are provided as a guide for comparison purposes only and no guarantee should be inferred from their inclusion. (Specimens measured in the dry state, 24 hours after moulding). |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRIMALLOY® B1922 | Mitsubishi Chemical Performance Polymers, Inc. | TPE | PRIMALLOY® |
| Spartech Polycom SC1F-4009U | Spartech Polycom | ABS | Spartech |
| Stylac™ R440T | Asahi Kasei Chemicals Corporation | AS | Stylac™ |
| Iupital® FU2050 | Mitsubishi Engineering-Plastics Corp | Acetal (POM) Copolymer | Iupital® |
| POLYfill PPHC GF3020 PB7 | Polykemi AB | PP, Unspecified | POLYfill |