Glass Fiber - Flame Retardant |
General Information | |
---|---|
Filler / Reinforcement |
|
Features |
|
RoHS Compliance |
|
Processing Method |
|
Physical | Nominal Value | Unit | Test Method |
---|---|---|---|
Specific Gravity | 1.53 | g/cm³ | ASTM D792 |
Molding Shrinkage - Flow (3.20 mm) | 0.40 - 0.60 | % | ASTM D955 |
Water Absorption (23°C, 24 hr) | 1.5 | % | ASTM D570 |
Moisture Content | 0.20 | % |
Additional Information | Nominal Value | Unit | |
---|---|---|---|
Primary Additive | 10 | % |
Hardness | Nominal Value | Unit | Test Method |
---|---|---|---|
Rockwell Hardness (R-Scale) | 116 | ASTM D785 |
Mechanical | Nominal Value | Unit | Test Method |
---|---|---|---|
Tensile Modulus | 6210 | MPa | ASTM D638 |
Tensile Strength | 89.6 | MPa | ASTM D638 |
Tensile Elongation (Yield) | 3.0 - 5.0 | % | ASTM D638 |
Flexural Modulus | 5170 | MPa | ASTM D790 |
Flexural Strength | 138 | MPa | ASTM D790 |
Impact | Nominal Value | Unit | Test Method |
---|---|---|---|
Notched Izod Impact (3.20 mm) | 75 | J/m | ASTM D256 |
Unnotched Izod Impact (3.20 mm) | 480 | J/m | ASTM D4812 |
Thermal | Nominal Value | Unit | Test Method |
---|---|---|---|
Deflection Temperature Under Load | ASTM D648 | ||
0.45 MPa, not annealed | 199 | °C | ASTM D648 |
1.8 MPa, not annealed | 182 | °C | ASTM D648 |
Electrical | Nominal Value | Unit | Test Method |
---|---|---|---|
Volume Resistivity | > 1.0E+14 | ohms·cm | ASTM D257 |
Dielectric Strength 1(in Oil) | 19 | kV/mm | ASTM D149 |
Dielectric Constant (1 MHz) | 3.80 | ASTM D150 | |
Dissipation Factor (1 MHz) | 0.017 | ASTM D150 |
Flammability | Nominal Value | Unit | Test Method |
---|---|---|---|
Flame Rating (1.50 mm, ** Values per RTP Company testing.) | V-0 | UL 94 |
Injection | Nominal Value | Unit | |
---|---|---|---|
Drying Temperature | 82.2 | °C | |
Drying Time | 2.0 | hr | |
Dew Point | -17.8 | °C | |
Processing (Melt) Temp | 243 - 279 | °C | |
Mold Temperature | 54.4 - 93.3 | °C | |
Injection Pressure | 68.9 - 103 | MPa |
Injection instructions |
---|
Desiccant Type Dryer Required. |
Note Message | |
---|---|
1 . | Method A (short time) |
Resin Grade | Manufacturer | Category | Trademark |
---|---|---|---|
SPESIN® KP212G30V0LG | Kolon Plastics, Inc. | PBT | SPESIN® |
VisiJet® M3 X | 3D Systems | Unspecified | VisiJet® |
Edgetek™ PC-20GF/000 FR NATURAL | PolyOne Corporation | PC | Edgetek™ |
EPO-TEK® H31D-LV | Epoxy Technology Inc. | Epoxy | EPO-TEK® |
Plaslube® HDPE GL5 | Techmer Engineered Solutions | HDPE | Plaslube® |