NORYL GTX™ GTX987 resin
| Category: | PPE+PS+Nylon , Polyphenylene Ether + PS + Nylon |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | NORYL GTX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bIWsGi_NORYL-GTX-GTX987-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Conductive GTX, CTE 7 |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.25 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (280°C/5.0 kg) | 8.5 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (280°C/5.0 kg) | 7.50 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 1.0 to 1.4 | % | Internal Method |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 3.0 | % | |
| Equilibrium, 23°C, 50% RH | 0.90 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 3250 | MPa | ASTM D638 |
| -- | 3000 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 55.0 | MPa | ASTM D638 |
| Yield | 62.0 | MPa | ISO 527-2/50 |
| Break 3 | 55.0 | MPa | ASTM D638 |
| Break | 62.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 4 | 5.0 | % | ASTM D638 |
| Yield | 5.0 | % | ISO 527-2/50 |
| Break 5 | 15 | % | ASTM D638 |
| Break | 20 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 2700 | MPa | ASTM D790 |
| -- 7 | 2800 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 90.0 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 95.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 11 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| -30°C | 70 | J/m | ASTM D256 |
| 23°C | 90 | J/m | ASTM D256 |
| -30°C 10 | 8.0 | kJ/m² | ISO 180/1A |
| 23°C 11 | 15 | kJ/m² | ISO 180/1A |
| Instrumented Dart Impact (23°C, Total Energy) | 10.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 185 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 12 | 190 | °C | ISO 75-2/Bf |
| Vicat Softening Temperature | |||
| -- | 192 | °C | ASTM D1525 13 |
| -- | 198 | °C | ISO 306/B50 |
| -- | 200 | °C | ISO 306/B120 |
| CLTE | |||
| Flow : -40 to 60°C | 5.5E-5 | cm/cm/°C | ASTM E831 |
| Flow : 23 to 60°C | 7.0E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 60°C | 6.0E-5 | cm/cm/°C | ASTM E831 |
| Transverse : 23 to 60°C | 7.5E-5 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 110 | °C | |
| Drying Time | 2.0 to 3.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 80.0 to 100 | °C | |
| Rear Temperature | 260 to 280 | °C | |
| Middle Temperature | 280 to 300 | °C | |
| Front Temperature | 300 to 320 | °C | |
| Nozzle Temperature | 280 to 300 | °C | |
| Processing (Melt) Temp | 300 to 320 | °C | |
| Mold Temperature | 100 to 120 | °C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 50 mm/min |
| 3 . | Type I, 50 mm/min |
| 4 . | Type I, 50 mm/min |
| 5 . | Type I, 50 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 sp=62mm |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 mm |
| 13 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tenite™ Butyrate 530A3720016 Clear, Trsp | Eastman Chemical Company | CAB | Tenite™ Butyrate |
| TORZEN® GT3300HSL BK20 | INVISTA Engineering Polymers | Nylon 66 | TORZEN® |
| Novablend™ 5075 | PolyOne Corporation | PVC, Rigid | Novablend™ |
| Desmopan® DP 2792A | Covestro - PUR | TPU-Polyester | Desmopan® |
| LNP™ THERMOCOMP™ Lexan_BFL2200 compound | SABIC Innovative Plastics Europe | PC | LNP™ THERMOCOMP™ |