RTP 6003-55A Z
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bHXVXP_RTP-6003-55A-Z.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Bondable to PC/PMMA, PC/PBT |
| General Information | |
|---|---|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.980 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 1.5 - 1.8 | % | ASTM D955 |
| Moisture Content | % |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peel Strength 1 | |||
| PC/PBT | 5.4 | kN/m | |
| PC/PMMA | 5.8 | kN/m |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 10 sec) | 55 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2(Yield, 3.20 mm) | 5.52 | MPa | ASTM D412 |
| Tensile Elongation 3(Yield) | 1000 | % | ASTM D412 |
| Tear Strength 4 | 30.6 | kN/m | ASTM D624 |
| Compression Set 5 | ASTM D395B | ||
| 23°C, 22 hr | 19 | % | ASTM D395B |
| 70°C, 22 hr | 65 | % | ASTM D395B |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 76.7 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Processing (Melt) Temp | 193 - 238 | °C | |
| Mold Temperature | 21.1 - 48.9 | °C | |
| Injection Pressure | 34.5 - 103 | MPa |
| Injection instructions |
|---|
| Desiccant Type Dryer Required. |
| Note Message | |
|---|---|
| 1 . | 90°, 20 in/min, RTP 55, Interface Failure |
| 2 . | C mold, 500 mm/min |
| 3 . | C mold, 500 mm/min |
| 4 . | C mould |
| 5 . | Type 2 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Topilene® HJ801R | Hyosung Corporation | PP Homopolymer | Topilene® |
| INTOL® 1783 | Versalis S.p.A. | SBR, Emulsion | INTOL® |
| IROGRAN® A 95 E 4813 | Huntsman Corporation | TPU-Polyester | IROGRAN® |
| Karina BLACK PVC COMPOUND -E 836-48/ 1-Y-CR | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LUVOCOM® 1301-8524-1 | Lehmann & Voss & Co. | PPS | LUVOCOM® |