ENGAGE™ 7270
| Category: | TPO (POE) , Polyolefin Elastomer |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | ENGAGE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bHQsBi_ENGAGE-7270.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ENGAGE™ 7270 Polyolefin Elastomer is a general-purpose copolymer designed to provide good cost/performance balance in polymer modification applications. Main Characteristics:
Applications:
|
| General Information | |
|---|---|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.880 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.80 | g/10 min | ASTM D1238 |
| Mooney Viscosity (ML 1+4, 121°C) | 24 | MU | ASTM D1646 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shore A, 1 sec, Compression Molded | 80 | ||
| Shore D, 1 sec, Compression Molded | 26 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus - 100% Secant 1(Compression Molded) | 3.70 | MPa | ASTM D638 |
| Tensile Strength 2(Break, Compression Molded) | 13.9 | MPa | ASTM D638 |
| Tensile Elongation 3(Break, Compression Molded) | 720 | % | ASTM D638 |
| Flexural Modulus | ASTM D790 | ||
| 1% Secant : Compression Molded | 22.5 | MPa | |
| 2% Secant : Compression Molded | 22.1 | MPa |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength 4 | 52.9 | kN/m | ASTM D624 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | -44.0 | °C | Internal Method |
| Vicat Softening Temperature | 50.0 | °C | ASTM D1525 |
| Melting Temperature (DSC) 5 | 64.0 | °C | Internal Method |
| Peak Crystallization Temperature (DSC) | 50.0 | °C | Internal Method |
| Note Message | |
|---|---|
| 1 . | 510 mm/min |
| 2 . | 510 mm/min |
| 3 . | 510 mm/min |
| 4 . | Die C |
| 5 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TORZEN® G3300HSL NC01 | INVISTA Engineering Polymers | Nylon 66 | TORZEN® |
| WPP TPO TPO7510UV-Black | Washington Penn Plastic Co. Inc. | TPO | WPP TPO |
| Adsyl 7572 XCP | LyondellBasell Industries | Polyolefin, Unspecified | Adsyl |
| HiFill® PA6/6 CC20 | Techmer Engineered Solutions | Nylon 66 | HiFill® |
| XENOY™ X4820 resin | SABIC Innovative Plastics | PC+PBT | XENOY™ |