Zytel® PLUS PLS95G35DH1 BK549
| Category: | Nylon, Unspecified , NYLON RESIN |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Zytel® PLUS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bGgGc9_ZytelPLUSPLS95G35DH1BK549.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 35% Glass Reinforced, Heat Stabilized, Polyamide |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.43 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Transverse flow | 0.70 | -- | % | ISO 294-4 |
| Flow | 0.20 | -- | % | ISO 294-4 |
| Water Absorption | ISO 62 | |||
| Saturated, 23°C, 2.00mm | 6.0 | -- | % | ISO 62 |
| Balance, 23°C, 2.00mm, 50% RH | 1.8 | -- | % | ISO 62 |
| Viscosity Number (96% H2SO4) | 130 | -- | cm³/g | ISO 307 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 11000 | 8000 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 200 | 140 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.3 | 6.0 | % | ISO 527-2 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -40°C | 12 | -- | kJ/m² | ISO 179/1eA |
| 23°C | 13 | 14 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 70 | 70 | kJ/m² | ISO 179/1eU |
| 23°C | 80 | 90 | kJ/m² | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 261 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 242 | -- | °C | ISO 75-2/A |
| Glass Transition Temperature 1 | 85.0 | -- | °C | ISO 11357-2 |
| Melting Temperature 2 | 265 | -- | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | |||
| Flow | 1.8E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Lateral | 7.2E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate 3(1.00 mm) | < 100 | -- | mm/min | ISO 3795 |
| Flammability Classification (1.5 mm) | HB | -- | IEC 60695-11-10, -20 | |
| FMVSS Flammability | B | -- | FMVSS 302 |
| Fill Analysis | Dry | Conditioned | Unit | |
|---|---|---|---|---|
| Specific Heat Capacity of Melt | 2300 | -- | J/kg/°C | |
| Thermal Conductivity of Melt | 0.22 | -- | W/m/K |
| Injection | Dry | Unit | |
|---|---|---|---|
| Melt Temperature, Optimum | 280 | °C | |
| Mold Temperature, Optimum | 100 | °C | |
| Drying Recommended | yes | ||
| Hold Pressure Time | 3.00 | s/mm | |
| Maximum Screw Tangential Speed | 200 | mm/sec |
| Fill Analysis | Dry | Conditioned | Unit | |
|---|---|---|---|---|
| Melt Density | 1.26 | -- | g/cm³ | |
| Ejection Temperature | 210 | -- | °C |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time - Desiccant Dryer | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Processing (Melt) Temp | 275 - 285 | °C | |
| Mold Temperature | 70 - 120 | °C | |
| Holding Pressure | 50.0 - 100 | MPa |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| 2 . | 10°C/min |
| 3 . | FMVSS 302 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Fainplast PVC MPH 92 | Fainplast Compounds S.r.l | PVC, Flexible | Fainplast PVC |
| Elvaloy® AC 1913 | DuPont Packaging & Industrial Polymers | EMA | Elvaloy® |
| LNP™ THERMOCOMP™ KF008 compound | SABIC Innovative Plastics Europe | Acetal (POM) Copolymer | LNP™ THERMOCOMP™ |
| Lumid® GP1300A(W) | LG Chem Ltd. | Nylon 6 | Lumid® |
| Sylvin 83009-60D Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |