INEOS HDPE K50-10-136
| Category: | HDPE Copolymer , High Density Polyethylene Copolymer |
| Manufacturer: | INEOS Olefins & Polymers USA |
| Trademark: | INEOS HDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bG7pi8_INEOS-HDPE-K50-10-136.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| K50-10-136 is a high molecular weight, high density polyethylene copolymer for blow molding automotive fuel tanks and under hood reservoirs. It combines excellent processability and outstanding physical performance, particularly environmental stress crack resistance (ESCR) and impact properties. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.950 | g/cm³ | ASTM D4883 |
| Melt Mass-Flow Rate (MFR) (190°C/21.6 kg) | 9.0 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance | |||
| 10% Igepal, F50 | 430 | hr | ASTM D1693A |
| 10% Igepal, F50 | 340 | hr | ASTM D1693B |
| 100% Igepal, F50 | > 1000 | hr | ASTM D1693A |
| 100% Igepal, F50 | > 1000 | hr | ASTM D1693B |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 63 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | ASTM D638 | ||
| Yield | 26.2 | MPa | |
| Break | 37.2 | MPa | |
| Tensile Elongation 2 | ASTM D638 | ||
| Yield | 9.9 | % | |
| Break | 850 | % | |
| Flexural Modulus | ASTM D790A | ||
| 2% Secant | 917 | MPa | |
| Tangent | 1230 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 450 | J/m | ASTM D256 |
| Notched Izod Impact (Area) | 44.0 | kJ/m² | ASTM D256 |
| Instrumented Impact, Ductility | ASTM D3763 | ||
| -30°C | Ductile | ||
| 23°C | Ductile |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 70.0 | °C | |
| 1.8 MPa, Unannealed | 47.8 | °C | |
| Brittleness Temperature | < -75.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 126 | °C | ASTM D1525 |
| Note Message | |
|---|---|
| 1 . | 51 mm/min |
| 2 . | 51 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCHULAMID® 6 MV HI | A. Schulman Europe | Nylon 6 | SCHULAMID® |
| AIE PET 40G3 | Asia International Enterprise (Hong Kong) Limited | PET | AIE PET |
| Beetle® PBTS830F | Teknor Apex Company (Chem Polymer) | PBT | Beetle® |
| BESTNYL SE25VI01AWX | Triesa Plastics | Nylon 66 | BESTNYL |
| COSMOPLENE® H101E | TPC, The Polyolefin Company (Singapore) Pte Ltd | PP Homopolymer | COSMOPLENE® |