EcoPaXX® Q170E-H
| Category: | Nylon 410 , Polyamide 410 |
| Manufacturer: | DSM Engineering Plastics |
| Trademark: | EcoPaXX® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bCVtSo_EcoPaXXQ170EH.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
EcoPaXX®Q170E-H is a Polyamide 410 (Nylon 410) material,. This product is available in North America, Europe or Asia Pacific. The processing method is extrusion. EcoPaXX®The main features of the Q170E-H are:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.09 | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 5.8 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 1.9 | % | ISO 62 |
| Viscosity Number | 170 | cm³/g | ISO 307 |
| Biomass Content- Bio C/Total C 1 | 70 | % | ASTM D6866 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3000 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 80.0 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | ||
| Yield | 4.6 | % | ISO 527-2 |
| Fracture | 20 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 4.0 | kJ/m² | ISO 179/1eA |
| 23°C | 5.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | No Break | ISO 179/1eU | |
| 23°C | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 175 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 75.0 | °C | ISO 75-2/A |
| Melting Temperature 2 | 250 | °C | ISO 11357-3 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 4.0 - 8.0 | hr | |
| Rear Temperature | 250 - 270 | °C | |
| Middle Temperature | 260 - 280 | °C | |
| Front Temperature | 270 - 290 | °C | |
| Nozzle Temperature | 270 - 300 | °C | |
| Processing (Melt) Temp | 270 - 300 | °C | |
| Mold Temperature | 60 - 100 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 3.00 - 10.0 | MPa | |
| Screw Compression Ratio | 2.5:1.0 |
| Note Message | |
|---|---|
| 1 . | Method B |
| 2 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCHULADUR® A GF 20 HF FR 1 | A. Schulman Europe | PBT | SCHULADUR® |
| SOLLAMID B 2720 | Krisoll Resinas Plásticas Ltda. | Nylon 6 | SOLLAMID |
| TARFLON™ AK3020 | Idemitsu Kosan Co., Ltd. | PC | TARFLON™ |
| Arak HDPE BL1 | Shazand (Arak) Petrochemical Corporation | HDPE | Arak HDPE |
| KEBAFORM® C 3090(K) | BARLOG plastics GmbH | Acetal (POM) Copolymer | KEBAFORM® C |