PRIMALENE WPP721
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Southern Polymer, Inc. |
| Trademark: | PRIMALENE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bBRs9v_PRIMALENE-WPP721.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
A narrow molecular weight high density polyethylene Applications:
Features:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.948 | g/cm³ | ASTM D4883 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 5.5 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance (10% Igepal, F50) | 24.0 | hr | ASTM D1693B |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 65 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 22.8 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 900 | % | ASTM D638 |
| Flexural Modulus | 965 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 64 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 76.7 | °C | ASTM D648 |
| Brittleness Temperature | < -75.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 128 | °C | ASTM D1525 |
| Note Message | |
|---|---|
| 1 . | 51 mm/min |
| 2 . | 51 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TITANLENE® LDF 260GG | Lotte Chemical Titan (M) Sdn. Bhd. | LDPE | TITANLENE® |
| ULTEM™ 4002 resin | SABIC Innovative Plastics | PEI | ULTEM™ |
| DIOSHY® MP-890PTA | DIOSHY Co.,Ltd. | SBS | DIOSHY® |
| Elastron® V P.V101.A30.B | Elastron USA, Inc. | TPV | Elastron® V |
| Hostacom X G3 U12 100000 | LyondellBasell Industries | PP Copolymer | Hostacom |