CYCOLOY™ CX7211 resin
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | CYCOLOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | b9RSkn_CYCOLOYCX7211resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| CYCOLOY CX7211 PC/ABS resin is a non-filled, injection moldable grade which has UL 94 rating at 2.5 mm 5VA. CYCOLOY CX7211 resin provides all color options and features an excellent balance of flow, impact and heat properties, which makes it an excellent candidate for thin wall applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.18 | g/cm³ | ASTM D792 |
| -- | 1.19 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (260°C/2.16 kg) | 16 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (260°C/2.16 kg) | 14.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.40 - 0.60 | % | Internal method |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.24 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.12 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2950 | MPa | ASTM D638 |
| -- | 2800 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 66.0 | MPa | ASTM D638 |
| Yield | 62.0 | MPa | ISO 527-2/50 |
| Fracture 3 | 60.0 | MPa | ASTM D638 |
| Fracture | 55.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 4 | 4.0 | % | ASTM D638 |
| Yield | 4.0 | % | ISO 527-2/50 |
| Fracture 5 | 98 | % | ASTM D638 |
| Fracture | 90 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0mm span 6 | 2750 | MPa | ASTM D790 |
| -- 7 | 2500 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 100 | MPa | ISO 178 |
| Yield, 50.0mm span 8 | 103 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9 | ISO 179/1eA | ||
| -30°C | 10 10 | kJ/m² | ISO 179/1eA |
| 23°C | 40 40 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength 10 | ISO 179/1eU | ||
| -30°C | No Break No Break | ISO 179/1eU | |
| 23°C | No Break No Break | ISO 179/1eU | |
| Notched Izod Impact | |||
| -30°C | 130 | J/m | ASTM D256 |
| 23°C | 630 | J/m | ASTM D256 |
| -30°C 11 | 10 10 | kJ/m² | ISO 180/1A |
| 23°C 12 | 40 40 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 13 | ISO 180/1U | ||
| -30°C | No Break No Break | ISO 180/1U | |
| 23°C | No Break No Break | ISO 180/1U | |
| Instrumented Dart Impact (23°C, Total Energy) | 60.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 94.0 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 6.40mm | 102 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.20mm | 89.0 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.40mm | 96.0 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 14 | 90.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | 105 | °C | ASTM D1525, ISO 306/B50, ISO 306/B120 15 |
| Ball Pressure Test (75°C) | Pass | IEC 60695-10-2 | |
| Linear thermal expansion coefficient | |||
| Flow : -40 to 40°C | 6.1E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 7.5E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : -40 to 40°C | 5.5E-5 | cm/cm/°C | ASTM E831 |
| Lateral : -40 to 40°C | 7.5E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | 0.20 | W/m/K | ISO 8302 |
| RTI Elec | 90.0 | °C | UL 746 |
| RTI Imp | 90.0 | °C | UL 746 |
| RTI | 90.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength | IEC 60243-1 | ||
| 0.800mm, in oil | 35 | kV/mm | IEC 60243-1 |
| 1.60mm, in oil | 25 | kV/mm | IEC 60243-1 |
| 3.20mm, in oil | 17 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index (CTI) | PLC 3 | UL 746 | |
| High Amp Arc Ignition (HAI) | PLC 0 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 2 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.25 mm | V-1 | UL 94 | |
| 1.50 mm | V-0 | UL 94 | |
| 2.00 mm | 5VB | UL 94 | |
| 2.50 mm | 5VA | UL 94 | |
| Glow Wire Flammability Index (1.00 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 1.00 mm | 800 | °C | IEC 60695-2-13 |
| 3.00 mm | 800 | °C | IEC 60695-2-13 |
| Oxygen Index | 32 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 - 87.8 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.040 | % | |
| Suggested Shot Size | 30 - 80 | % | |
| Rear Temperature | 221 - 254 | °C | |
| Middle Temperature | 221 - 266 | °C | |
| Front Temperature | 243 - 277 | °C | |
| Nozzle Temperature | 243 - 277 | °C | |
| Processing (Melt) Temp | 243 - 277 | °C | |
| Mold Temperature | 60.0 - 82.2 | °C | |
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 40 - 70 | rpm | |
| Vent Depth | 0.038 - 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type 1, 50mm/min |
| 3 . | Type 1, 50mm/min |
| 4 . | Type 1, 50mm/min |
| 5 . | Type 1, 50mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 sp=62mm |
| 10 . | 80*10*4 sp=62mm |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 |
| 13 . | 80*10*4 |
| 14 . | 80*10*4 mm |
| 15 . | 标准 B (120°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP ESD C 1200-80A | RTP Company | TPU-Polyester | RTP |
| ELASTOSIL® RT 426 | Wacker Chemie AG | Silicone | ELASTOSIL® RT |
| Hifax TRC 103P R299 | LyondellBasell Industries | PP Impact Copolymer | Hifax |
| LNP™ THERMOCOMP™ EXTC8270 compound | SABIC Innovative Plastics Asia Pacific | PBT | LNP™ THERMOCOMP™ |
| Luran® S 797SE | Styrolution | ASA | Luran® S |