Ultraform® S 1320 003

Category:	Acetal (POM) Copolymer , Acetal (POM) Copolymer
Manufacturer:	BASF Corporation
Trademark:	Ultraform®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	b9NGrq_Ultraform-S-1320-003.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message
Free-flowing, rapidly solidifying grade for moldings difficult to produce by injection molding and having low wall thickness; increased stiffness and heat distortion resistance.

General Information
Features	Rigid, good Copolymer Good liquidity
Uses	Thin wall parts
Agency Ratings	EC 1907/2006 (REACH)
RoHS Compliance	RoHS compliance
Forms	Particles
Processing Method	Injection molding
Multi-Point Data	Isochronous Stress vs. Strain (ISO 11403-1) Isothermal Stress vs. Strain (ISO 11403-1) Secant Modulus vs. Strain (ISO 11403-1) Shear Modulus vs. Temperature (ISO 11403-1) Specific Heat vs. Temperature (ISO 11403-2) Specific Volume vs Temperature (ISO 11403-2) Viscosity vs. Shear Rate (ISO 11403-2)
Resin ID (ISO 1043)	POM

Physical	Nominal Value	Unit	Test Method
Density	1.41	g/cm³	ISO 1183
Apparent Density	0.85	g/cm³
Melt Volume-Flow Rate (MVR) (190°C/2.16 kg)	11.0	cm³/10min	ISO 1133
Molding Shrinkage			ISO 294-4
Vertical flow direction	2.1	%	ISO 294-4
Flow direction	2.1	%	ISO 294-4
Water Absorption			ISO 62
Saturated, 23°C	0.80	%	ISO 62
Equilibrium, 23°C, 50% RH	0.20	%	ISO 62

Hardness	Nominal Value	Unit	Test Method
Ball Indentation Hardness (H 358/30)	165	MPa	ISO 2039-1

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	3000	MPa	ISO 527-2
Tensile Stress (Yield)	68.0	MPa	ISO 527-2/50
Tensile Strain (Yield)	9.0	%	ISO 527-2/50
Nominal Tensile Strain at Break	25	%	ISO 527-2/50
Tensile Creep Modulus ¹(1000 hr)	1450	MPa	ISO 899-1

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength			ISO 179/1eA
-30°C	5.5	kJ/m²	ISO 179/1eA
23°C	5.5	kJ/m²	ISO 179/1eA
Charpy Unnotched Impact Strength			ISO 179/1eU
-30°C	170	kJ/m²	ISO 179/1eU
23°C	170	kJ/m²	ISO 179/1eU

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature (1.8 MPa, Unannealed)	100	°C	ISO 75-2/A
Melting Temperature	171	°C	ISO 11357-3
CLTE - Flow (23 to 55°C)	1.1E-4	cm/cm/°C	ISO 11359-2
Maximum operating temperature- short cycle operation	100	°C

Additional Information	Nominal Value		Test Method
Automotive Materials (> 1.00 mm)	Passed		FMVSS 302
ISO Type	POM-K, M-GNR, 04-002		ISO 9988-1

Injection	Nominal Value	Unit
Screw Speed		mm/sec

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity	1.0E+15	ohms	IEC 60093
Volume Resistivity	1.0E+15	ohms·cm	IEC 60093
Relative Permittivity (1 MHz)	3.70		IEC 60250
Dissipation Factor (1 MHz)	5.0E-3		IEC 60250
Comparative Tracking Index (Solution A)	600	V	IEC 60112

Flammability	Nominal Value	Unit	Test Method
Flame Rating (1.60 mm)	HB		UL 94

Injection	Nominal Value	Unit
Drying Temperature	100	°C
Drying Time	3.0	hr
Suggested Max Moisture	0.20	%
Hopper Temperature	200	°C
Rear Temperature	200	°C
Middle Temperature	200	°C
Front Temperature	200	°C
Nozzle Temperature	200	°C
Processing (Melt) Temp	190 - 230	°C
Mold Temperature	60.0 - 120	°C

Injection instructions
Residence Time : <10 min

Note Message
1 .	strain <= 0,5%, 23°C

Resin Grade	Manufacturer	Category	Trademark
TECHNO ABS 541	Techno Polymer Co, Ltd.	ABS	TECHNO ABS
Starpylen MK001AS	Eurostar Engineering Plastics	PP, Unspecified	Starpylen
Thermoset Plastics SC-104	Thermoset, Lord Chemical Products	Silicone	Thermoset Plastics
Petlon R-Prime F3-T20-00-BK	Petlon Polymers Ltd	PP, Unspecified	Petlon R-Prime
Sylvin 9067-90 White 1353	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin