AURAMID PA6GF35BK ULT
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Aurora Manufacturing Ltd |
| Trademark: | AURAMID |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | b9LlZp_AURAMID-PA6GF35BK-ULT.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA6GF35BK ULT is a general purpose 35% glass filled PA6 black compound manufactured from recycled polymer, containing a high performance mould release / processing additive system. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Recycled Content |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.37 | g/cm³ | ISO 1183 |
| Molding Shrinkage | 0.30 to 0.50 | % | |
| Water Absorption (23°C, 24 hr) | 1.1 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ISO 2039-2 | |
| Shore Hardness (Shore D) | 86 | ISO 868 | |
| Ball Indentation Hardness (H 961/30) | 195 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | > 145 | MPa | ISO 527-2 |
| Tensile Strain (Break) | < 3.0 | % | ISO 527-2 |
| Flexural Modulus | 7500 | MPa | ISO 178 |
| Flexural Stress | 210 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | > 8.5 | kJ/m² | ISO 179/B |
| Notched Izod Impact Strength | > 6.5 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | > 200 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | > 180 | °C | ISO 75-2/A |
| Melting Temperature (DSC) 1 | 218 | °C | ISO 3146 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+13 | ohms | IEC 60093 |
| Electric Strength (2.00 mm) | 22 | kV/mm | IEC 60243-1 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | < 100 | mm/min | FMVSS 302 |
| Flame Rating | HB | Internal Method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 to 80.0 | °C | |
| Rear Temperature | 215 to 260 | °C | |
| Middle Temperature | 215 to 260 | °C | |
| Front Temperature | 215 to 260 | °C | |
| Mold Temperature | 80.0 | °C |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Anjacom® R050/75S Black 91010 | Almaak International GmbH | PC+ABS | Anjacom® |
| Durethan® BKV 50 G H2.0 EF 000000 | LANXESS GmbH | Nylon 6 | Durethan® |
| Hostacom HKC 465T | LyondellBasell Industries | PP Homopolymer | Hostacom |
| INTEGRAL™ 816 | The Dow Chemical Company | Polyolefin, Unspecified | INTEGRAL™ |
| Hostacom PPU X9067HS 156505 | LyondellBasell Industries | PP Copolymer | Hostacom |