Sumitomo Epoxy E 8354A-1
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Sumitomo Bakelite North America, Inc. |
| Trademark: | Sumitomo Epoxy |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | b9KBit_Sumitomo-Epoxy-E-8354A-1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| E 8354A-1 is a fiberglass and mineral reinforced epoxy molding compound, with excellent dimensional stability, good electrical insulation properties, and good strength. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 2.04 | g/cm³ | ASTM D792 |
| Apparent Density | 0.80 | g/cm³ | ASTM D1895 |
| Molding Shrinkage - Flow | 0.20 to 0.30 | % | ASTM D955 |
| Water Absorption - 48 hr (50°C) | 0.20 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 88.0 | MPa | ASTM D638 |
| Flexural Modulus | 20000 | MPa | ASTM D790 |
| Flexural Strength (Break) | 149 | MPa | ASTM D790 |
| Compressive Strength | 260 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 34 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Annealed) | 275 | °C | ASTM D648 |
| CLTE - Flow | 2.2E-5 | cm/cm/°C | ASTM E831 |
| RTI Elec | 130 | °C | UL 746 |
| RTI Imp | 130 | °C | UL 746 |
| RTI Str | 130 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength 1 | ASTM D149 | ||
| -- 2 | 15 | kV/mm | |
| -- 3 | 14 | kV/mm | |
| Dielectric Constant 4(1 MHz) | 4.40 | ASTM D150 | |
| Dissipation Factor 5(1 MHz) | 0.015 | ASTM D150 | |
| Arc Resistance | 185 | sec | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | V-0 | UL 94 |
| Note Message | |
|---|---|
| 1 . | 60 Hz, Wet |
| 2 . | Method A (Short-Time) |
| 3 . | Method B (Step-by-Step) |
| 4 . | Wet |
| 5 . | Wet |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 200D GB 20 | RTP Company | Nylon 612 | RTP |
| Vi-Chem PVC VNC95-80E-8804 | Vi-Chem Corporation | PVC, Rigid | Vi-Chem PVC |
| WPP PP PPH1CF4-Black | Washington Penn Plastic Co. Inc. | PP Homopolymer | WPP PP |
| 4LAC® 10H23100 A-M | 4Plas | ABS | 4LAC® |
| Ecomass® 5100TU96 | Ecomass Technologies | SEBS | Ecomass® |