Generic PP, Unspecified - Glass Fiber
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | b96MiE_Generic-PP-Unspecified---Glass-Fiber.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic PP, Unspecified - Glass Fiber This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 0.933 - 1.25 | g/cm³ | ASTM D792 |
| 23°C | 1.04 - 1.13 | g/cm³ | ISO 1183 |
| -- | 0.960 - 1.23 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) | |||
| 230°C/2.16 kg | 1.9 - 12 | g/10 min | ASTM D1238 |
| 230°C/2.16 kg | 0.20 - 13 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (230°C/2.16 kg) | 3.00 - 18.2 | cm³/10min | ISO 1133 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.17 - 0.84 | % | ASTM D955 |
| Transverse flow : 23°C | 0.77 - 1.2 | % | ASTM D955 |
| 23°C | 0.12 - 2.0 | % | ISO 294-4 |
| Water Absorption | |||
| 23°C, 24 hr | 7.0E-3 - 0.032 | % | ASTM D570 |
| 23°C, 24 hr | 0.025 - 0.10 | % | ISO 62 |
| Saturated, 23°C | 0.020 | % | ASTM D570 |
| Equilibrium, 23°C | 0.020 - 1.5 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| 23°C | 83 - 117 | ASTM D785 | |
| 23°C | 98 - 110 | ISO 2039-2 | |
| Durometer Hardness (23°C) | 70 - 76 | ASTM D2240 | |
| Ball Indentation Hardness | 85.0 - 125 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 2020 - 9050 | MPa | ASTM D638 |
| 23°C | 2890 - 9280 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 34.2 - 93.5 | MPa | ASTM D638 |
| Yield, 23°C | 23.4 - 104 | MPa | ISO 527-2 |
| Fracture, 23°C | 26.9 - 120 | MPa | ASTM D638 |
| Fracture, 23°C | 1.95 - 111 | MPa | ISO 527-2 |
| 23°C | 32.4 - 91.5 | MPa | ASTM D638 |
| 23°C | 52.3 - 119 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield, 23°C | 1.5 - 10 | % | ASTM D638 |
| Yield, 23°C | 1.8 - 4.7 | % | ISO 527-2 |
| Fracture, 23°C | 1.0 - 6.0 | % | ASTM D638 |
| Fracture, 23°C | 1.5 - 6.7 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 1970 - 6980 | MPa | ASTM D790 |
| 23°C | 1640 - 6980 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 34.4 - 141 | MPa | ASTM D790 |
| 23°C | 35.6 - 157 | MPa | ISO 178 |
| Yield, 23°C | 41.2 - 145 | MPa | ASTM D790 |
| Fracture, 23°C | 148 - 150 | MPa | ASTM D790 |
| Compressive Strength (23°C) | 44.1 - 51.4 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.9 - 16 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 19 - 59 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 25 - 120 | J/m | ASTM D256 |
| 23°C | 3.0 - 14 | kJ/m² | ISO 180 |
| Unnotched Izod Impact | |||
| 23°C | 180 - 660 | J/m | ASTM D256 |
| 23°C | 19 - 46 | kJ/m² | ISO 180 |
| Instrumented Dart Impact | |||
| 23°C | 3.70 - 17.4 | J | ASTM D3763 |
| 23°C | 1.70 - 2.21 | J | ISO 6603-2 |
| Dart Drop Impact (23°C) | 0.226 - 0.347 | J | ASTM D3029 |
| Dart Drop Impact (23°C) | 0.205 - 0.572 | J | ASTM D5420 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 148 - 164 | °C | ASTM D648 |
| 0.45 MPa, not annealed | 130 - 164 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 119 - 155 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 118 - 162 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 118 - 161 | °C | ASTM D1525 |
| -- | 110 - 167 | °C | ISO 306 |
| Melting Temperature | |||
| -- | 160 - 183 | °C | |
| -- | 159 - 162 | °C | ISO 3146 |
| Linear thermal expansion coefficient | |||
| Flow | 3.0E-5 - 5.6E-5 | cm/cm/°C | ASTM D696 |
| Flow | 7.0E-6 - 1.1E-4 | cm/cm/°C | ISO 11359-2 |
| Lateral | 4.4E-5 - 1.3E-4 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity (23°C) | 0.22 - 0.34 | W/m/K | ASTM C177 |
| RTI Elec | 65.0 - 120 | °C | UL 746 |
| RTI Imp | 65.0 - 120 | °C | UL 746 |
| RTI | 65.0 - 120 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | |||
| -- | 5.1E+2 - 1.3E+16 | ohms | ASTM D257 |
| -- | 2.0E+2 - 1.0E+16 | ohms | IEC 60093 |
| Volume Resistivity | |||
| 23°C | 1.0E+3 - 1.3E+16 | ohms·cm | ASTM D257 |
| 23°C | 12 - 1.0E+17 | ohms·cm | IEC 60093 |
| Dielectric Strength | |||
| 23°C | 19 - 41 | kV/mm | ASTM D149 |
| 23°C | 17 - 61 | kV/mm | IEC 60243-1 |
| Dielectric Constant (23°C) | 2.30 - 3.30 | ASTM D150 | |
| Dissipation Factor (23°C) | 1.0E-3 - 1.2E-3 | ASTM D150 | |
| Arc Resistance | 80.0 - 130 | sec | ASTM D495 |
| Comparative Tracking Index | 595 - 650 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glow Wire Flammability Index | 844 - 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | 650 - 960 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 69.7 - 100 | °C | |
| Drying Time | 1.4 - 4.0 | hr | |
| Suggested Max Moisture | 0.048 - 0.053 | % | |
| Suggested Max Regrind | 15 | % | |
| Rear Temperature | 197 - 230 | °C | |
| Middle Temperature | 212 - 236 | °C | |
| Front Temperature | 214 - 248 | °C | |
| Nozzle Temperature | 215 - 246 | °C | |
| Processing (Melt) Temp | 209 - 240 | °C | |
| Mold Temperature | 39.0 - 62.8 | °C | |
| Injection Pressure | 5.52 - 97.1 | MPa | |
| Holding Pressure | 4.48 - 46.4 | MPa | |
| Back Pressure | 0.150 - 1.25 | MPa | |
| Screw Speed | 44 - 57 | rpm | |
| Cushion | 8.89 - 8.91 | mm |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic PP, Unspecified - Glass FiberThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Syncure™ V0030G RoHS | PolyOne Corporation | XLPE | Syncure™ |
| Zytel® 101L NC010 | DuPont Performance Polymers | Nylon 66 | Zytel® |
| FERREX® GPP20CS51BK | Ferro Corporation | PP, Unspecified | FERREX® |
| TOTAL Polyethylene Lumicene® M 3410 EP (EU - Blow Molding) | TOTAL Refining & Chemicals | mMDPE | TOTAL Polyethylene |
| Moplen HP552R | LyondellBasell Industries | PP Homopolymer | Moplen |