Nymax™ X GMF 604 40 UV Black 148 rev 4
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Nymax™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | b90k1P_Nymax-X-GMF-604-40-UV-Black-148-rev-4.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Nymaxm®GMF600 series polymer products are a combination of nylon 6 resin and glass fiber or mineral reinforcement, which can maintain a unique balance between physical properties and component properties. These materials are dedicated to processing in standard thermoplastic processing equipment. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.48 | g/cm³ | ASTM D792 |
| -- | 1.49 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow | 0.20 - 0.40 | % | ASTM D955 |
| -- | 0.20 - 0.30 | % | ISO 294-4 |
| Water Absorption | |||
| 24 hr, 3.18 mm | 0.80 | % | ASTM D570 |
| 23°C, 24 hr | 1.0 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- | 8270 | MPa | ASTM D638 |
| -- | 8500 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield 1 | 121 | MPa | ASTM D638 |
| Yield | 117 | MPa | ISO 527-2 |
| Fracture 2 | 117 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Fracture 3 | 2.0 - 3.0 | % | ASTM D638 |
| Fracture | 2.5 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 7580 | MPa | ASTM D790 |
| -- | 8400 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 179 | MPa | ASTM D790 |
| -- | 190 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C, 3.18mm, injection molding | 69 | J/m | ASTM D256A |
| -- | 13 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Annealed) | 195 | °C | ISO 75-2/A |
| Additional Information |
|---|
| Molded Test Bars: Dry as Molded |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Mold Temperature | 60.0 - 107 | °C |
| Note Message | |
|---|---|
| 1 . | Type 1, 5.1 mm/min |
| 2 . | Type 1, 5.1 mm/min |
| 3 . | Type 1, 5.1 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 227 FR NH | RTP Company | Nylon 66 | RTP |
| Ferro PP TPP40AJ26UL-TN | Ferro Corporation | PP, Unspecified | Ferro PP |
| ELASTOSIL® RT 774 | Wacker Chemie AG | Silicone | ELASTOSIL® RT |
| Laprene® 83K000999 | SO.F.TER. SPA | SEBS | Laprene® |
| Jampilen HP561R | Jam Polypropylene Company | PP Homopolymer | Jampilen |