HANWHA EVA 1633

Category:	EVA , Ethylene Vinyl Acetate Copolymer
Manufacturer:	Hanwha Chemical
Trademark:	HANWHA EVA
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	b8sUDR_HANWHA-EVA-1633.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
HANWHA EVA 1633 designed for extrusion process is manufactured with exhaustive inspection to be used as a solar cell encapsulant. Specially, EVA 1633 is consistent with customer demands to meet a quality of solar modules. Higher VA contents to ensure good optical and adhesion properties Optimized processablity for producing EVA sheet in a extrusion equipment. Improved yellowing resistance and cross-linking efficiency compared with conventional grades

Message

HANWHA EVA 1633 designed for extrusion process is manufactured with exhaustive inspection to be used as a solar cell encapsulant. Specially, EVA 1633 is consistent with customer demands to meet a quality of solar modules.

Higher VA contents to ensure good optical and adhesion properties

Optimized processablity for producing EVA sheet in a extrusion equipment.

Improved yellowing resistance and cross-linking efficiency compared with conventional grades

General Information
Features	Copolymer Good Adhesion Good Processability
Uses	Solar Panels
Agency Ratings	FDA 21 CFR 177.1350(a)(1)
Forms	Pellets
Processing Method	Extrusion Sheet Extrusion

Physical	Nominal Value	Unit	Test Method
Density	0.955	g/cm³	ASTM D1505
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	30	g/10 min	ASTM D1238
Vinyl Acetate Content	33.0	wt%	Internal Method

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength (Break)	7.16	MPa	ASTM D638
Tensile Elongation (Break)	840	%	ASTM D638

Thermal	Nominal Value	Unit	Test Method
Brittleness Temperature	< -76.0	°C	ASTM D746
Vicat Softening Temperature	< 30.0	°C	ASTM D1525
Melting Temperature	64.0	°C	ASTM D3417

Resin Grade	Manufacturer	Category	Trademark
RTP 1201-55D	RTP Company	TPU-Polyester	RTP
TUFNYL® RST 80 NATURAL	SRF Ltd.	Nylon 66	TUFNYL®
Formolene® HB5502S1	Formosa Plastics Corporation, U.S.A.	HDPE	Formolene®
Geon™ Vinyl Dry Blend E1501	PolyOne Corporation	PVC, Rigid	Geon™ Vinyl Dry Blend
Infino FD-1106	LOTTE ADVANCED MATERIALS CO., LTD.	PC	Infino