Generic PVC Alloy
| Category: | PVC Alloy , Polyvinyl Chloride Alloy |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | b89KYf_Generic-PVC-Alloy.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic PVC Alloy This information is provided for comparative purposes only. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.15 - 1.49 | g/cm³ | ASTM D792 |
| Spiral Flow | 58.4 - 87.0 | cm | |
| Molding Shrinkage - Flow (23°C) | 0.35 - 0.36 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (23°C) | 60 - 80 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 1890 - 2420 | MPa | ASTM D638 |
| Tensile Strength (Yield, 23°C) | 29.6 - 46.6 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 15 - 380 | % | ASTM D638 |
| Flexural Modulus (23°C) | 1890 - 2840 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 48.3 - 93.1 | MPa | ASTM D790 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength (23°C) | 8.00 - 71.9 | kN/m | ASTM D624 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 27 - 960 | J/m | ASTM D256 |
| Drop Impact Resistance (23°C) | 50.4 - 178 | J/cm | ASTM D4226 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Volume (23°C) | -26 - -0.30 | % | ASTM D471 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 76.0 - 90.6 | °C | ASTM D648 |
| 0.45 MPa, annealed | 83.9 - 92.4 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 72.4 - 85.1 | °C | ASTM D648 |
| 1.8 MPa, annealed | 73.0 - 88.0 | °C | ASTM D648 |
| CLTE - Flow | 3.0E-5 - 1.4E-4 | cm/cm/°C | ASTM D696 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 204 - 207 | °C |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic PVC AlloyThis information is provided for comparative purposes only. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 184 - 199 | °C |
| Extrusion instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic PVC AlloyThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Nanjing Hongrui PA66 A304 | Nanjing Hongrui Engineering Plastics Co., Ltd. | Nylon 66 | Nanjing Hongrui PA66 |
| BESTNYL SE00VI01AS08 | Triesa Plastics | Nylon 66 | BESTNYL |
| Fiberfil® J-60/30/E/M | Fiberfil® Engineered Plastics Inc. | PP Homopolymer | Fiberfil® |
| Geon™ Vinyl Flexible 86155 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| Karina CLEAR PVC COMPOUND 60/200 | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |