LNP STAT-KON AE002 is a compound based on ABS resin containing 10% Carbon Fiber. Added feature of this material is: Electrically Conductive. Also known as: LNP* STAT-KON* Compound AC-1002 Product reorder name: AE002 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.16 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.20 to 0.40 | % | |
| Across Flow : 24 hr | 0.30 to 0.50 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.23 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.35 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 7650 | MPa | ASTM D638 |
| -- | 7380 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 86.1 | MPa | ASTM D638 |
| Yield | 82.0 | MPa | ISO 527-2/5 |
| Break 3 | 83.3 | MPa | ASTM D638 |
| Break | 82.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 1.5 | % | ASTM D638 |
| Yield | 1.4 | % | ISO 527-2/5 |
| Break 5 | 1.5 | % | ASTM D638 |
| Break | 1.4 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 6660 | MPa | ASTM D790 |
| -- 7 | 6510 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 112 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 114 | MPa | ASTM D790 |
| Break, 50.0 mm Span 9 | 108 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 48 | J/m | ASTM D256 |
| 23°C 10 | 4.9 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 230 | J/m | ASTM D4812 |
| 23°C 11 | 15 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 9.70 | J | ASTM D3763 |
| -- | 2.20 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 105 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 12 | 105 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 101 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 13 | 101 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 3.3E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 8.3E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 2.0 to 4.0 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 to 0.10 | % | |
| Rear Temperature | 204 to 216 | °C | |
| Middle Temperature | 232 to 243 | °C | |
| Front Temperature | 266 to 277 | °C | |
| Processing (Melt) Temp | 260 | °C | |
| Mold Temperature | 71.1 to 82.2 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 1.3 mm/min |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 mm |
| 13 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 200 GB 60 | RTP Company | Nylon 66 | RTP |
| Zhongfa PP pp7 | Yuyao Zhongfa Engineering Plastics Co. Ltd. | PP, Unspecified | Zhongfa |
| ASI POLYPROPYLENE 1901-01 | A. Schulman Inc. | PP Homopolymer | ASI POLYPROPYLENE |
| Generic ABS+PC - Stainless Steel Fiber | Generic | PC+ABS | Generic |
| DEXFLEX® D60-UV 4LLA | LyondellBasell Industries | TPO (POE) | DEXFLEX® |