| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| UL File Number |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.53 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.10 | % | |
| Across Flow | 1.0 | % | |
| Water Absorption (23°C, 24 hr) | 0.020 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ASTM D785 | ||
| M-Scale | 98 | ||
| R-Scale | 118 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 19000 | MPa | ASTM D638 |
| Tensile Strength | 170 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 1.1 | % | ASTM D638 |
| Flexural Modulus | 18000 | MPa | ASTM D790 |
| Flexural Strength | 270 | MPa | ASTM D790 |
| Compressive Strength | 200 | MPa | ASTM D695 |
| Poisson's Ratio | 0.35 | ||
| Coefficient of Friction 1 | ASTM D1894 | ||
| vs. Steel - Dynamic | 0.23 | ||
| vs. Steel - Static | 0.23 | ||
| Flexural Elongation at Break | 1.6 | % | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 55 | J/m | ASTM D256 |
| Unnotched Izod Impact | 320 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 265 | °C | ASTM D648 |
| CLTE | ASTM D696 | ||
| Flow : -30 to 90°C | 1.4E-5 | cm/cm/°C | |
| Transverse : -30 to 90°C | 1.4E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+2 to 1.0E+3 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.800 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 290 to 320 | °C | |
| Middle Temperature | 290 to 320 | °C | |
| Front Temperature | 290 to 320 | °C | |
| Mold Temperature | 120 to 150 | °C |
| Note Message | |
|---|---|
| 1 . | P=150KPa, V=0.3m/s |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TOTAL Polypropylene PPH 9059 | TOTAL Refining & Chemicals | PP Homopolymer | TOTAL Polypropylene |
| ELASTOSIL® LR 3071/30 A/B | Wacker Chemie AG | Silicone | ELASTOSIL® LR |
| KOPHOS® KO1370 | Kolon Plastics, Inc. | PC | KOPHOS® |
| Karina IVORY PVC COMPOUND 900-35/2-P-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| TAFMER™ XM-5070S | Mitsui Chemicals, Inc. | PAO | TAFMER™ |