LNP™ THERMOCOMP™ YF005 compound
| Category: | TPEE , Thermoplastic Polyester Elastomer |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | b6GKWa_LNP-THERMOCOMP-YF005-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP YF005 is a compound based on Polyester Elastomer resin containing 25% Glass Fiber. Also known as: LNP* THERMOCOMP* Compound YF-1005 Product reorder name: YF005 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.40 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.50 to 0.70 | % | |
| Across Flow : 24 hr | 1.0 to 3.0 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.31 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.41 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2370 | MPa | ASTM D638 |
| -- | 2360 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 47.0 | MPa | ASTM D638 |
| Yield | 46.0 | MPa | ISO 527-2/5 |
| Break 3 | 46.0 | MPa | ASTM D638 |
| Break | 45.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 9.9 | % | ASTM D638 |
| Yield | 9.5 | % | ISO 527-2/5 |
| Break 5 | 8.3 | % | ASTM D638 |
| Break | 10 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 1980 | MPa | ASTM D790 |
| -- 7 | 2120 | MPa | ISO 178 |
| Flexural Stress | 53.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 330 | J/m | ASTM D256 |
| 23°C 8 | 29 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 1000 | J/m | ASTM D4812 |
| 23°C 9 | 76 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 15.7 | J | ASTM D3763 |
| -- | 7.80 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 186 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 10 | 180 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 152 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 11 | 142 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 3.6E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 1.8E-4 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Rear Temperature | 182 to 193 | °C | |
| Middle Temperature | 204 to 216 | °C | |
| Front Temperature | 227 to 238 | °C | |
| Processing (Melt) Temp | 216 to 238 | °C | |
| Mold Temperature | 26.7 to 54.4 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 mm |
| 11 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SEPTON™ 4099 | Kuraray Co., Ltd. | SEEPS | SEPTON™ |
| Wellamid® GF13-66 XE-NBK1 | Wellman Engineering Resins | Nylon 66 | Wellamid® |
| NYLOY® NG-1050N | Nytex Composites Co., Ltd. | Nylon 6 | NYLOY® |
| Laser+® HS CF746A (D53A) | DAK Americas LLC | PET | Laser+® |
| Isoplast® 302EZ TPU | Lubrizol Advanced Materials, Inc. | ETPU | Isoplast® |