Beetle® PBTB130F Datasheet,PBT+PET,Teknor Apex Company (Chem Polymer)-SHANGHAI SUSHENG

Message
PBTB130F is a 30% glass fibre reinforced PBT injection moulding grade. It features a modified formulation that offers good mechanical performance combined with higher surface gloss and excellent mould release.

General Information
Filler / Reinforcement	Glass fiber reinforced material, 30% filler by weight
Features	Highlight Thermal stability, good Good demoulding performance Excellent appearance
Forms	Particle
Processing Method	Injection molding
Resin ID (ISO 1043)	PBT+PET-GF30

Physical	Nominal Value	Unit	Test Method
Density	1.55	g/cm³	ISO 1183
Molding Shrinkage ¹	0.60 - 1.2	%	Internal method
Water Absorption (Equilibrium, 23°C, 50% RH)	0.060	%	ISO 62

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	10000	MPa	ISO 527-2
Tensile Stress (Yield)	140	MPa	ISO 527-2
Tensile Strain (Break)	2.5	%	ISO 527-2
Flexural Modulus	9300	MPa	ISO 178
Flexural Stress	200	MPa	ISO 178

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength	11	kJ/m²	ISO 179
Charpy Unnotched Impact Strength	45	kJ/m²	ISO 179
Notched Izod Impact	7.0	kJ/m²	ISO 180

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature
0.45 MPa, not annealed	> 200	°C	ISO 75-2/B
1.8 MPa, not annealed	200	°C	ISO 75-2/Af

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity	1.0E+16	ohms	IEC 60093
Volume Resistivity	1.0E+14	ohms·cm	IEC 60093
Dielectric Strength (3.00 mm)	16	kV/mm	IEC 60243-1
Relative Permittivity	3.30		IEC 60250
Comparative Tracking Index	300	V	IEC 60112

Flammability	Nominal Value	Unit	Test Method
Flame Rating (1.50 mm, Teknor Apex test result)	HB		UL 94
Oxygen Index	20	%	ISO 4589-2

Injection	Nominal Value	Unit
Drying Temperature	120	°C
Drying Time	4.0	hr
Rear Temperature	240 - 270	°C
Middle Temperature	245 - 270	°C
Front Temperature	250 - 270	°C
Processing (Melt) Temp	260 - 275	°C
Mold Temperature	80.0 - 110	°C
Injection Rate	Fast
Screw Speed	50 - 200	rpm

Injection instructions
Back Pressure: LowInjection Pressure: HighPolyester grades are very sensitive to moisture content during processing. Suitable pre-drying is essential. Excess moisture causes rapid hydrolytic degradation of the melt and severe impairment of mechanical properties. Low melt viscosity & brittle product are often the key indicators. Vacuum or dehumidified air driers must be used.

Note Message
1 .	Mould shrinkage is significantly influenced by many factors including wall thickness, gating, moulding shape and processing conditions. The range values given are determined from specimen bar mouldings of 1.5mm to 4mm wall thickness. They are provided as a guide for comparison purposes only and no guarantee should be inferred from their inclusion. (Specimens measured in the dry state, 24 hours after moulding).

Note Message

1 .

Mould shrinkage is significantly influenced by many factors including wall thickness, gating, moulding shape and processing conditions. The range values given are determined from specimen bar mouldings of 1.5mm to 4mm wall thickness. They are provided as a guide for comparison purposes only and no guarantee should be inferred from their inclusion. (Specimens measured in the dry state, 24 hours after moulding).

Category:	PBT+PET , Polybutylene Terephthalate + PET
Manufacturer:	Teknor Apex Company (Chem Polymer)
Trademark:	Beetle®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	b5zMn5_Beetle-PBTB130F.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
Vitaster® UW36NT6757	Jackdaw Polymers	PBT+PET	Vitaster®
NuSil MED-9011	NuSil Technology	Silicone	NuSil
Di-Pak™ E-4541-3	Hapco Inc.	TP, Unspecified	Di-Pak™
Iupital® FT2010	Mitsubishi Engineering-Plastics Corp	Acetal (POM) Copolymer	Iupital®
Sylvin 9302-70 FU White 1326	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin