Huafon EP625
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Huafon Group Co., Ltd. |
| Trademark: | Huafon |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | b3sFw9_Huafon-EP625.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
EP625 is a high-end Nylon 66 resin for engineering plastics. This resin offers a well—balanced combination of engineering properties characterized by high strength and dimension stability; good flow, surface lubricity and cold resistance. Typical Properties EP625 is especially suitable for demanding injection molding flow properties and fire resistance. Terminal applications mainly in machinery, electronics, electrical, instrumentation, automotive components, railway, home appliances, communications, cable ties and precision engineering products, etc., EP625 also can be used for the production of medical equipment, sporting goods, daily necessities and so on. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (275°C/2.16 kg) | 90 | g/10 min | ISO 1133 |
| Particle Size | 1.40 to 2.00 | g/100 pellets | Internal Method |
| Relative Viscosity | 2.50 to 2.60 | Internal Method | |
| Water Content | < 2500 | mg/kg | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 1 | 76.1 | MPa | ISO 527-2 |
| Tensile Strain 2(Break) | 55 | % | ISO 527-2 |
| Flexural Modulus 3 | 2640 | MPa | ISO 178 |
| Flexural Stress 4 | 99.8 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 5(23°C) | 6.1 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 6 | |||
| 0.45 MPa, Annealed | 192 | °C | ISO 75-2/B |
| 1.8 MPa, Annealed | 66.4 | °C | ISO 75-2/A |
| Vicat Softening Temperature 7 | 240 | °C | ISO 306/B120 |
| Peak Melting Temperature 8 | 266 | °C | ASTM D3418 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating 9 | UL 94 | ||
| 1.00 mm | V-2 | ||
| 1.60 mm | V-2 | ||
| 3.00 mm | V-2 |
| Note Message | |
|---|---|
| 1 . | 48h/23°C/50%RH |
| 2 . | 48h/23°C/50%RH |
| 3 . | 48h/23°C/50%RH |
| 4 . | 48h/23°C/50%RH |
| 5 . | 48h/23°C/50%RH |
| 6 . | 48h/23°C/50%RH |
| 7 . | 48h/23°C/50%RH |
| 8 . | 10°C/min |
| 9 . | 48h/23°C/50%RH |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SNOLEN® EF 0.25/52 | JSC Gazprom neftekhim Salavat | HDPE | SNOLEN® |
| Dynaflex™ G2706-1000-00 | PolyOne Corporation | TPE | Dynaflex™ |
| Hiprolon® 11 ECN Black H8L P40 | Arkema | Nylon 1012 | Hiprolon® |
| Hostalen CRP 100 black (XL) | LyondellBasell Industries | HDPE | Hostalen |
| ESTOPLAST EP 4020WR24 | Ester Industries Ltd. | PBT | ESTOPLAST EP |