| Sevrene® 4000-75A is a Polyvinyl Chloride material. It is available in North America. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.11 | g/cm³ | ISO 1183 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore A, 15 sec) | 75 | ISO 868 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 1(100% Strain) | 2.90 | MPa | ISO 37 |
| Tensile Stress 2(Break) | 8.90 | MPa | ISO 37 |
| Tensile Elongation 3(Break) | 950 | % | ISO 37 |
| Tear Strength 4 | 38 | kN/m | ISO 34-1 |
| Compression Set (70°C, 22 hr) | 39 | % | ISO 815 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air (100°C, 1008 hr) | -2.0 | % | SAE J2236 |
| Change in Tensile Strain at Break (100°C, 1008 hr) | 4.0 | % | SAE J2236 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature 5 | -50.0 | °C | ISO 974 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Fogging (85°C) 6 | 95 | % | GM 9305P |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| Arizona Weathering 7 | SAE J1976 | ||
| Color Change, Delta E | 1.15 | ||
| Surface Defects | No Objectionable Defects | ||
| Florida Weathering 8 | SAE J1976 | ||
| Color Change, Delta E | 0.970 | ||
| Surface Defects | No Objectionable Defects | ||
| Xenon Arc | |||
| Color Change, Delta E 9 | 1.87 | SAE J1885 | |
| Color Change, Delta E 10 | 1.56 | SAE J1960 | |
| Surface Defects 11 | No Objectionable Defects | SAE J1960 | |
| Surface Defects 12 | No Objectionable Defects | SAE J1885 |
| Note Message | |
|---|---|
| 1 . | 500 mm/min |
| 2 . | 500 mm/min |
| 3 . | 500 mm/min |
| 4 . | Method Ba, Angle (Unnicked), 500 mm/min |
| 5 . | Type B |
| 6 . | Type B, 6 hr |
| 7 . | 2 years, Natural Exposure, Exterior |
| 8 . | 2 years, Natural Exposure, Exterior |
| 9 . | 1240 kJ/m, Interior |
| 10 . | 2500 kJ/m², Exterior |
| 11 . | 2500 kJ/m², Exterior |
| 12 . | 1240 kJ/m, Interior |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mirakutoran® TPU P190 | Japan Mirakutoran Inc. | TPU Alloy | Mirakutoran® TPU |
| SKYBOND® 562 | Industrial Summit Technology Co. | API | SKYBOND® |
| Boda BDT2461E | Chenguang Fluoro & Silicone Elastomers Co., Ltd. | Fluorelastomer | Boda |
| ExxonMobil™ HDPE HTA 001HP2 | ExxonMobil Chemical | HDPE, HMW | ExxonMobil™ HDPE |
| EcoLon® GF1978-BK1 | Wellman Engineering Resins | Nylon 66 | EcoLon® |