Plaslube® J-1/30/TF/15
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Techmer Engineered Solutions |
| Trademark: | Plaslube® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | b0Ps7l_Plaslube-J-1-30-TF-15.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Plaslube®J-1/30/TF/15 is a polyamide 66 (nylon 66) product, which contains a 30% glass fiber reinforced material. It can be processed by injection molding and is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. Typical application areas are: engineering/industrial accessories. Features include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | ||||
| -- | 1.52 | -- | g/cm³ | ASTM D792 |
| -- | 1490 | -- | kg/m³ | ISO 1183 1 |
| Molding Shrinkage - Flow (3.18 mm) | 0.20 | -- | % | ASTM D955 |
| Water Absorption | ||||
| 24 hr | 0.60 | -- | % | ASTM D570 |
| Saturation | 5.3 | -- | % | ISO 62 2 |
| Balance | 1.4 | -- | % | ISO 62 3 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale) | 119 | -- | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 9000 | 7200 | MPa | ISO 527-2 4 |
| Tensile Stress | ||||
| Fracture | 160 | 130 | MPa | ISO 527-2 5 |
| -- | 159 | -- | MPa | ASTM D638 |
| Tensile Elongation | ||||
| Fracture | 2.5 | -- | % | ASTM D638 |
| Fracture | 2.5 | 4.5 | % | ISO 527-2 6 |
| Flexural Modulus (23°C) | 9310 | -- | MPa | ASTM D790 |
| Flexural Strength | ASTM D790 | |||
| -- | 238 | -- | MPa | ASTM D790 |
| Fracture, 23°C | 238 | -- | MPa | ASTM D790 |
| Compressive Strength | 193 | -- | MPa | ASTM D695 |
| Shear Strength | 68.9 | -- | MPa | ASTM D732 |
| Coefficient of Friction | ASTM D1894 | |||
| With steel-dynamic | 0.25 | -- | ASTM D1894 | |
| With steel-static | 0.20 | -- | ASTM D1894 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA 7 | |||
| -30°C | 7.00 | -- | kJ/m² | ISO 179/1eA |
| 23°C | 10.0 | 18.0 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact (23°C, 3.18 mm) | 130 | -- | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ||||
| 0.45 MPa, not annealed | 260 | -- | °C | ASTM D648 |
| 0.45 MPa | 260 | -- | °C | ISO 75-2 8 |
| 1.8 MPa, not annealed | 254 | -- | °C | ASTM D648 |
| 1.8 MPa | 250 | -- | °C | ISO 75-2 9 |
| Melting Temperature 10 | 260 | -- | °C | ISO 11357-3 11 |
| CLTE - Flow | 4.3E-5 | -- | cm/cm/°C | ASTM D696 |
| RTI Elec (1.47 mm) | 65.0 | -- | °C | UL 746 |
| RTI Imp (1.47 mm) | 65.0 | -- | °C | UL 746 |
| RTI (1.47 mm) | 65.0 | -- | °C | UL 746 |
| Flammability | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Flame Rating (1.59 mm) | HB | -- | UL 94 | |
| Burning Behav. at 1.6mm nom. thickn. (1.50 mm, UL) | HB | -- | ISO 1210 12 | |
| Burning Behav. at thickness h (1.50 mm, UL) | HB | -- | ISO 1210 13 |
| Additional Information |
|---|
| 干燥 Coefficient of Friction, Static, Thrust washer, 40psi, ambient temp.: 0.20Coefficient of Friction, Dynamic, Thrust washer, 40psi, 50 ft/min, ambient temp.: 0.25Limiting PV, Thrust washer, 100 FPM, ambient temperature: 2E4Compressive Strength, ASTM D695, 73°F: 28000 psi |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.12 | % | |
| Rear Temperature | 282 - 293 | °C | |
| Middle Temperature | 288 - 299 | °C | |
| Front Temperature | 277 - 288 | °C | |
| Nozzle Temperature | 282 - 293 | °C | |
| Processing (Melt) Temp | 282 - 304 | °C | |
| Mold Temperature | 54.4 - 93.3 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.345 - 0.689 | MPa |
| Injection instructions |
|---|
| Screw Speed: MediumRecommendations for Molding and Tool Conditions: Well ventedMoisture Content, as received: Product is packaged at 0.2% or less.Recomended Max Moisture: 0.12% down to 0.08% |
| Note Message | |
|---|---|
| 1 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 2 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 3 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 4 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 5 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 6 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 7 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 8 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 9 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 10 . | 10 °C/min |
| 11 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 12 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 13 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® C4640 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| Sylvin 2906-85C Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| BioSpan® F SPU | DSM Biomedical Inc. | PUR, Unspecified | BioSpan® |
| LCA® N66-33GF | UniPlas, Inc. | Nylon 66 | LCA® |
| Lupoy® 1302HP-07 | LG Chem Ltd. | PC | Lupoy® |