TRISTAR® PC-10R-CL(V15)

Category:	PC , Polycarbonate
Manufacturer:	Polymer Technology and Services, LLC
Trademark:	TRISTAR®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	b03snP_TRISTAR-PC-10R-CL-V15-.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

TRISTAR®PC-10R-CL(V15) is a polycarbonate (PC) product,. It can be processed by injection molding and is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. TRISTAR®The application fields of PC-10R-CL(V15) include electrical/electronic applications and wire and cable.

Features include:

flame retardant/rated flame

Comply with REACH standard

ROHS certification

Good UV resistance

mold release agent

General Information
Additive	demoulding UV stabilizer
Features	Good UV resistance Good demoulding performance
Uses	Electrical/Electronic Applications Communication Equipment
Agency Ratings	EC 1907/2006 (REACH)
RoHS Compliance	RoHS compliance
Appearance	Clear/transparent
Forms	Particle
Processing Method	Injection molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.20	g/cm³	ASTM D792
Melt Mass-Flow Rate (MFR) (300°C/1.2 kg)	15	g/10 min	ASTM D1238
Water Absorption (23°C, 24 hr)	0.15	%	ASTM D570

Hardness	Nominal Value	Unit	Test Method
Rockwell Hardness (R-Scale)	118		ASTM D785

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength (Yield, 3.17 mm)	62.1	MPa	ASTM D638
Tensile Elongation (Break, 3.17 mm)	150	%	ASTM D1708
Flexural Modulus (3.17 mm)	2410	MPa	ASTM D790
Flexural Strength (Yield, 3.17 mm)	96.5	MPa	ASTM D790

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact (3.17 mm)	850	J/m	ASTM D256

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load
1.8 MPa, not annealed	127	°C	ASTM D648
1.8 MPa, not annealed	137	°C	ISO 75-2/A
Linear thermal expansion coefficient			ASTM E831
Flow : -40 to 95°C	7.0E-5	cm/cm/°C	ASTM E831
Lateral : -40 to 95°C	6.8E-5	cm/cm/°C	ASTM E831
RTI Elec	125	°C	UL 746
RTI Imp	115	°C	UL 746
RTI	125	°C	UL 746

Electrical	Nominal Value	Unit	Test Method
Arc Resistance	PLC 6		ASTM D495
Comparative Tracking Index (CTI)	PLC 2		UL 746
High Amp Arc Ignition (HAI)			UL 746
1.50 mm	PLC 0		UL 746
3.00 mm	PLC 1		UL 746
High Voltage Arc Tracking Rate (HVTR)	PLC 3		UL 746
Hot-wire Ignition (HWI)			UL 746
1.50 mm	PLC 3		UL 746
3.00 mm	PLC 2		UL 746

Flammability	Nominal Value	Unit	Test Method
Flame Rating (1.50 mm)	V-2		UL 94
Glow Wire Flammability Index	960	°C	IEC 60695-2-12
Glow Wire Ignition Temperature	775	°C	IEC 60695-2-13

Optical	Nominal Value	Unit	Test Method
Refractive Index	1.586		ASTM D542
Transmittance ¹	89.0	%	ASTM D1003
Haze	1.0	%	ASTM D1003

Injection	Nominal Value	Unit
Drying Temperature	121	°C
Drying Time	3.0 - 4.0	hr
Drying Time, Maximum	48	hr
Suggested Shot Size	40 - 60	%
Rear Temperature	249 - 271	°C
Middle Temperature	260 - 271	°C
Front Temperature	271 - 288	°C
Nozzle Temperature	266 - 282	°C
Processing (Melt) Temp	277 - 293	°C
Mold Temperature	71.1 - 93.3	°C
Injection Pressure	68.9 - 124	MPa
Back Pressure	0.345 - 1.38	MPa
Screw Speed	40 - 70	rpm
Clamp Tonnage	2.8 - 6.9	kN/cm²

Injection instructions
Injection Speed - Edge Gate: Slow to MediumInjection Speed - Tab Gate: Medium to FastInjection Speed - Tunnel Gate: Fast

Note Message
1 .	Visible

Resin Grade	Manufacturer	Category	Trademark
Mineralblend® PP-1800	Colour Image Plastic Compound Sdn. Bhd. (CIPC)	PP Homopolymer	Mineralblend®
Chemlon® 130 BH	Teknor Apex Company (Chem Polymer)	Nylon 66	Chemlon®
Fainplast PVC MPH 64	Fainplast Compounds S.r.l	PVC, Flexible	Fainplast PVC
Karina IVORY PVC COMPOUND IRDB 40-LF-BR(CABELAUTO)	Karina Ind. e Com. de Plásticos Ltda	PVC, Unspecified	Karina
HIFOR Xtreme® SC74859	Westlake Chemical Corporation	LLDPE	HIFOR Xtreme®