GUR® 4113
| Category: | UHMWPE , Ultra High Molecular Weight Polyethylene |
| Manufacturer: | Celanese Corporation |
| Trademark: | GUR® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | azvfCH_GUR-4113.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| GUR 4113 UHMW-PE is a linear polyolefin in powder form with a molecular weight of approximately 3.9 MM g/mol calculated using Margolies' equation. This resin has good abrasion resistance, low frictional properties and a high notched impact strength of > 170 kJ/m2. The resin is normally used for compression molding of thin sheets. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 0.928 | g/cm³ | ASTM D792 |
| -- | 0.940 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | |||
| 190°C/21.6 kg | < 0.10 | g/10 min | ASTM D1238 |
| 190°C/21.6 kg | < 1.0 | g/10 min | ISO 1133 |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | < 0.010 | % | |
| Equilibrium, 23°C, 50% RH | < 0.010 | % | |
| Viscosity Number | 2000 | cm³/g | ISO 307 |
| Elongational Stress F - 150/10 | 0.130 | MPa | ISO 1152-2 |
| Intrinsic Viscosity | 18 | dl/g | ISO 1628-3 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Abrasion Loss | 110 | Internal Method | |
| Wear by Sandslurry Method 1 | 110 | Internal Method |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Impact Strength 2 | 170 | kJ/m² | ISO 1152-2 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | |||
| Shore D | 64 | ASTM D2240 | |
| Shore D, 15 sec | 62 | ISO 868 | |
| Ball Indentation Hardness 3 | 38.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 750 | MPa | ISO 527-2/1A/1 |
| Tensile Strength | |||
| Yield, 23°C | 21.4 | MPa | ASTM D638 |
| Yield | 17.0 | MPa | ISO 527-2/1A/50 |
| Tensile Strain (Yield) | 20 | % | ISO 527-2/1A/50 |
| Nominal Tensile Strain at Break | > 50 | % | ISO 527-2/1A/50 |
| Tensile Creep Modulus | ISO 899-1 | ||
| 1 hr | 450 | MPa | |
| 1000 hr | 250 | MPa | |
| Coefficient of Friction (vs. Steel - Dynamic) | 0.10 | Internal Method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 65.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 42.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 80.0 | °C | ASTM D1525, ISO 306/B50 |
| CLTE - Flow | 2.0E-4 | cm/cm/°C | ASTM D696, ISO 11359-2 |
| Specific Heat | Internal Method | ||
| -- | 1840 | J/kg/°C | |
| 23°C | 1840 | J/kg/°C | |
| Thermal Conductivity (23°C) | 0.41 | W/m/K | Internal Method |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | |||
| -- | > 1.0E+13 | ohms | ASTM D257 |
| -- | > 1.0E+12 | ohms | IEC 60093 |
| Volume Resistivity | |||
| -- | > 1.0E+15 | ohms·cm | ASTM D257 |
| -- | > 1.0E+14 | ohms·cm | IEC 60093 |
| Electric Strength | 45 | kV/mm | IEC 60243-1 |
| Dielectric Constant | |||
| 1 MHz | 3.00 | ASTM D150, IEC 60250 | |
| 100 Hz | 2.10 | IEC 60250 | |
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 3.9E-4 | ||
| 1 MHz | 1.0E-3 | ||
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | Based on GUR 4120=100 |
| 2 . | 14° V-notch both sides |
| 3 . | 30 sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MORETEC™ V-0398CN | Prime Polymer Co., Ltd. | LLDPE | MORETEC™ |
| VITAMIDE® BF13GR6598 | Jackdaw Polymers | Nylon 6 | VITAMIDE® |
| Borealis PP WD955CF | Borealis AG | Polyolefin, Unspecified | Borealis PP |
| Geon™ Vinyl Rigid Molding M5015 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Rigid Molding |
| Karina BEIGE PVC COMPOUND -E 841-08/184-Y-ERYB | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |