Ultramid 8200 HS is a heat stabilized, medium viscosity, PA6 injection molding homopolymer, exhibiting resistance to sink-mark formation in thick sections, and improved toughness over conventional lower viscosity grades. It possesses a combination of strength, stiffness and toughness properties as well as excellent heat, chemical and abrasion resistance. It is available in natural and pigmented versions. Applications Ultramid 8200 HS is generally receommended for application such as wiring devices, plugs, receptacles, gears, connectors, convoluted tubing, filter housings, hinges, and textile components.

General Information
Additive	Heat Stabilizer
Features	Good Abrasion Resistance Good Chemical Resistance Good Stiffness Good Strength Good Toughness Heat Stabilized High Heat Resistance Homopolymer Medium Viscosity
Uses	Connectors Filters Gears Housings Plugs Textile Applications Tubing Wire & Cable Applications
Agency Ratings	EC 1907/2006 (REACH)
RoHS Compliance	RoHS Compliant
Appearance	Colors Available Natural Color
Forms	Pellets
Processing Method	Injection Molding

Physical	Dry	Conditioned	Unit	Test Method
Specific Gravity	1.13	--	g/cm³	ASTM D792, ISO 1183
Molding Shrinkage - Flow (3.18 mm)	1.2	--	%
Water Absorption
24 hr	1.6	--	%	ASTM D570
23°C, 24 hr	1.6	--	%	ISO 62
Saturation	9.5	--	%	ASTM D570
Saturation, 23°C	9.5	--	%	ISO 62
Equilibrium, 50% RH	2.7	--	%	ASTM D570
Equilibrium, 23°C, 50% RH	2.7	--	%	ISO 62

Hardness	Dry	Conditioned	Unit	Test Method
Rockwell Hardness (R-Scale)	119	--		ASTM D785

Mechanical	Dry	Conditioned	Unit	Test Method
Tensile Modulus (23°C)	2700	--	MPa	ISO 527-2
Tensile Strength
Yield, -40°C	136	120	MPa	ASTM D638, ISO 527-2
Yield, 23°C	85.0	39.0	MPa	ASTM D638
Yield, 121°C	23.0	--	MPa	ASTM D638, ISO 527-2
Yield, 23°C	80.0	39.0	MPa	ISO 527-2
Tensile Elongation
Yield, -40°C	3.0	3.0	%	ASTM D638
Yield, 23°C	20	16	%	ASTM D638
Yield, 121°C	15	--	%	ASTM D638
Yield, 23°C	5.0	16	%	ISO 527-2
Break, -40°C	8.0	4.0	%	ASTM D638
Break, 23°C	60	> 100	%	ASTM D638
Break, 121°C	> 100	--	%	ASTM D638
Nominal Tensile Strain at Break (23°C)	25	> 50	%	ISO 527-2
Flexural Modulus
-40°C	3010	3660	MPa	ASTM D790
23°C	2830	740	MPa	ASTM D790
65°C	460	--	MPa	ASTM D790
90°C	350	--	MPa	ASTM D790
121°C	305	--	MPa	ASTM D790
23°C	2400	--	MPa	ISO 178
Flexural Strength
-40°C	168	161	MPa	ASTM D790
23°C	110	37.0	MPa	ASTM D790
65°C	30.0	--	MPa	ASTM D790
90°C	20.0	--	MPa	ASTM D790
121°C	18.0	--	MPa	ASTM D790
23°C	82.0	--	MPa	ISO 178

Impact	Dry	Conditioned	Unit	Test Method
Charpy Notched Impact Strength (23°C)	3.5	--	kJ/m²	ISO 179
Charpy Unnotched Impact Strength (23°C)	No Break	--		ISO 179
Notched Izod Impact				ASTM D256
-40°C	48	43	J/m
23°C	65 J/m	No Break

Thermal	Dry	Conditioned	Unit	Test Method
Deflection Temperature Under Load
0.45 MPa, Unannealed	175	--	°C	ASTM D648
1.8 MPa, Unannealed	65.0	--	°C	ASTM D648
1.8 MPa, Unannealed	60.0	--	°C	ISO 75-2/A
Peak Melting Temperature	220	--	°C	ASTM D3418, ISO 3146
CLTE - Flow	8.3E-5	--	cm/cm/°C	ASTM E831
RTI Elec				UL 746
0.710 mm	130	--	°C
1.30 mm	130	--	°C
3.00 mm	130	--	°C
6.00 mm	130	--	°C
RTI Imp				UL 746
0.710 mm	95.0	--	°C
1.30 mm	105	--	°C
3.00 mm	105	--	°C
6.00 mm	105	--	°C
RTI Str				UL 746
0.710 mm	95.0	--	°C
1.30 mm	105	--	°C
3.00 mm	105	--	°C
6.00 mm	105	--	°C

Flammability	Dry	Conditioned	Test Method
Flame Rating			UL 94
3.00 mm	V-2	--
6.00 mm	V-2	--

Category:	Nylon 6 , Polyamide 6
Manufacturer:	BASF Corporation
Trademark:	Ultramid®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	aznZLv_Ultramid-8200-HS.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
Rhelon G1533H-00	RheTech, Inc.	Nylon 6	Rhelon
TES J-1200/20/VO/Natl	Techmer Engineered Solutions	ABS	TES
WELLAMID Nylon 6600 GV 45 HWCP	CP-Polymer-Technik GmbH & Co. KG	Nylon 66	WELLAMID Nylon
Elvaloy® AC 3217	DuPont Packaging & Industrial Polymers	EnBA	Elvaloy®
IROGRAN® A 70 H 4714 M	Huntsman Corporation	TPU-Polyester	IROGRAN®