Lionpol LC-61550
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | Lion Polymers Incorporated |
| Trademark: | Lionpol |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ayrgbu_Lionpol-LC-61550.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Lionpol LC-61550 is a thermoplastic elastomer (TPE) product,. It is available in North America. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 15 | g/10 min | ASTM D1238 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 1.4 - 1.5 | % | ASTM D955 |
| Transverse flow | 1.4 - 1.5 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 50 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (100% Strain) | 1.10 | MPa | ASTM D412 |
| Tensile Strength (Break) | 9.20 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 1100 | % | ASTM D412 |
| Compression Set | ASTM D395 | ||
| 70°C, 22 hr | 37 | % | ASTM D395 |
| 100°C, 22 hr | 53 | % | ASTM D395 |
| Additional Information |
|---|
| Permanent Set: 8% |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 182 - 193 | °C | |
| Front Temperature | 199 - 210 | °C | |
| Nozzle Temperature | 216 - 221 | °C | |
| Mold Temperature | 37.8 - 60.0 | °C | |
| Back Pressure | 0.552 - 1.03 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TYRIL™ 867 E | Trinseo | SAN | TYRIL™ |
| CONATHANE® EN-2523 | Cytec Industries Inc. | PUR, Unspecified | CONATHANE® |
| Gallonprene® GP540-7504(n)F | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| Edgetek™ ET3200-8001 LG | PolyOne Corporation | PC | Edgetek™ |
| Hetron™ FR 1540 | Ashland Performance Materials | Vinyl Ester | Hetron™ |