Visituf™ 3020
| Category: | PC , Polycarbonate |
| Manufacturer: | Technical Polymers, LLC |
| Trademark: | Visituf™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ayg9oX_Visituf-3020.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Visituf™3020 is a polycarbonate (PC) material,. This product is available in North America and is processed by injection molding. Visituf™The main features of the 3020 are:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 20 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (23°C) | 72.4 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 100 | % | ASTM D638 |
| Flexural Modulus (23°C) | 2280 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 93.1 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 770 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 141 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 131 | °C | ASTM D648 |
| Vicat Softening Temperature | 149 | °C | ASTM D1525 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+18 | ohms·cm | ASTM D257 |
| Additional Information |
|---|
| Tensile Elongation, ASTM D638: >100% |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 104 - 121 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Processing (Melt) Temp | 271 - 316 | °C | |
| Mold Temperature | 65.6 - 104 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 25 - 100 | rpm | |
| Clamp Tonnage | 4.1 - 5.5 | kN/cm² | |
| Cushion | 3.18 - 6.35 | mm | |
| Screw L/D Ratio | 20.0:1.0 | ||
| Screw Compression Ratio | 2.0:1.0 to 2.5:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RONFALIN® VE100 | A. Schulman Europe | ABS | RONFALIN® |
| Sinvicomp SGH5000P | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Sinvicomp |
| Sylvin 9703-90 Red 6274 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Cri-Line SP-510-55 | Cri-Tech, Inc. | Fluorelastomer | Cri-Line |
| Eltex® Superstress™ CAP508S3 | INEOS Olefins & Polymers Europe | HDPE Copolymer | Eltex® |