Susteel® G-10
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | TOSOH Corporation |
| Trademark: | Susteel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | aw33w4_Susteel-G-10.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Glass fiber and mineral filled / Standard grade |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.94 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (315°C/5.0 kg) | 90 | g/10 min | ASTM D1238 |
| Molding Shrinkage | Internal Method | ||
| Flow | 0.30 | % | |
| Across Flow | 0.60 | % | |
| Water Absorption (Equilibrium) | > 0.020 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 121 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 116 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 0.60 | % | ASTM D638 |
| Flexural Modulus | 20000 | MPa | ASTM D790 |
| Flexural Strength | 221 | MPa | ASTM D790 |
| Tensile Weld Strength | 39.0 | MPa | ASTM D638 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Bar Flow Length (1.00 mm) | 125 | mm | Internal Method |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 64 | J/m | ASTM D256 |
| Unnotched Izod Impact | 210 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | > 260 | °C | ASTM D648 |
| Melting Temperature | 285 | °C | Internal Method |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+18 | ohms·cm | ASTM D257 |
| Dielectric Strength | 15 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 4.90 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 1.5E-3 | ASTM D150 | |
| Arc Resistance | 150 | sec | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 to 150 | °C | |
| Drying Time | 2.0 to 5.0 | hr | |
| Rear Temperature | 270 to 300 | °C | |
| Middle Temperature | 270 to 300 | °C | |
| Nozzle Temperature | 290 to 330 | °C | |
| Mold Temperature | 135 to 150 | °C | |
| Injection Pressure | 50.0 to 150 | MPa | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 1.00 to 20.0 | MPa | |
| Screw Speed | 100 to 150 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Idemitsu PS NS-221 | Idemitsu PS | PS (HIPS) | Idemitsu PS |
| POLYfill PPH GF3030 PD2 | Polykemi AB | PP Homopolymer | POLYfill |
| Polyrocks EP8400X105V-1 | Polyrocks Chemical Co., Ltd | XLPE | Polyrocks |
| NYLOY® NG-0820B | Nytex Composites Co., Ltd. | Nylon 6 | NYLOY® |
| Kepital® TC3020 | Korea Engineering Plastics Co., Ltd | Acetal (POM) Copolymer | Kepital® |