| Polyamide 6 Compound resin, mineral reinforced grade |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.45 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.20 - 0.50 | % | ASTM D955 |
| Water Absorption (Equilibrium, 23°C, 60% RH) | 0.50 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 118 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (23°C) | 83.0 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 5.5 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 4800 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 127 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 34 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 200 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 175 | °C | ASTM D648 |
| Peak Melting Temperature | 220 | °C | ASTM D3418 |
| CLTE - Flow | 4.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength | 22 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 3.50 | ASTM D150 | |
| Arc Resistance | 130 | sec | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxxam™ MX5200-5005 RS BLACK | PolyOne Corporation | PP Homopolymer | Maxxam™ |
| SynPlast™ DOP-N | PolyOne Corporation | Di (2-ethylhexyl) Phthalate | SynPlast™ |
| Sylvin 8983-85 White 1196 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| UMG ABS® PS-507 | UMG ABS, Ltd. | ABS | UMG ABS® |
| NOVADURAN® 5010GN6-30M8X | Mitsubishi Engineering-Plastics Corp | PBT | NOVADURAN® |