LNP™ THERMOCOMP™ 4X08423 compound
| Category: | PFA , Perfluoroalkoxy |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | atb0l4_LNP-THERMOCOMP-4X08423-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP 4X08423 is a compound based on PFA resin containing Glass Fiber. Also known as: LNP* THERMOCOMP* Compound 4X08423 Product reorder name: 4X08423 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | ASTM D792 | ||
| -- | 2.19 | g/cm³ | |
| -- | 2.20 | g/cm³ | |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 2.0 to 4.0 | % | |
| Across Flow : 24 hr | 2.0 to 4.0 | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.010 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 4670 | MPa | ASTM D638 |
| -- | 4610 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 40.0 | MPa | ASTM D638 |
| Yield | 40.0 | MPa | ISO 527-2/5 |
| Break 3 | 36.0 | MPa | ASTM D638 |
| Break | 39.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 3.3 | % | ASTM D638 |
| Yield | 3.3 | % | ISO 527-2/5 |
| Break 5 | 3.6 | % | ASTM D638 |
| Break | 3.4 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 3300 | MPa | ASTM D790 |
| -- 7 | 4380 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 60.0 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 49.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 260 | J/m | ASTM D256 |
| 23°C 9 | 23 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 590 | J/m | ASTM D4812 |
| 23°C 10 | 45 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 10.9 | J | ASTM D3763 |
| -- | 4.80 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 297 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 11 | 259 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 243 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 12 | 158 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 5.2E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 8.9E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 149 | °C | |
| Drying Time | 4.0 | hr | |
| Drying Time, Maximum | 4.0 | hr | |
| Hopper Temperature | 43.0 | °C | |
| Rear Temperature | 360 | °C | |
| Middle Temperature | 360 | °C | |
| Front Temperature | 360 | °C | |
| Nozzle Temperature | 366 | °C | |
| Processing (Melt) Temp | 360 | °C | |
| Mold Temperature | 149 | °C | |
| Back Pressure | 3.50 | MPa | |
| Screw Speed | 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 mm |
| 12 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2101 TFE 15 | RTP Company | PEI | RTP |
| TARFLON™ NEO AG1950 | Idemitsu Kosan Co., Ltd. | PC | TARFLON™ |
| Unichem 5511-02 | Colorite Polymers | PVC, Unspecified | Unichem |
| Electrafil® J-1200/CF/20 | Techmer Engineered Solutions | ABS | Electrafil® |
| Karina CLEAR CRYSTAL PVC COMP. -E 85/201-DA-IS-SI-AT | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |