LNP™ VERTON™ MX02795 compound
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ VERTON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | aqkLeQ_LNP-VERTON-MX02795-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP VERTON MX02795 is a compound based on Polypropylene resin containing Proprietary Fillers. Added features of this material include: Heat Stabilized, UV Stabilized, Structural. Also known as: LNP* VERTON* Compound PDX-M-02795 Product reorder name: MX02795 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.21 | g/cm³ | ASTM D792 |
| -- | 1.19 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.30 | % | ASTM D955 |
| Across Flow : 24 hr | 0.50 | % | ASTM D955 |
| Across Flow : 24 hr | 0.53 | % | ISO 294-4 |
| Flow : 24 hr | 0.27 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 8960 | MPa | ASTM D638 |
| -- | 9570 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 118 | MPa | ASTM D638 |
| Yield | 111 | MPa | ISO 527-2 |
| Break | 118 | MPa | ASTM D638 |
| Break | 122 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 2.2 | % | ASTM D638 |
| Yield | 2.1 | % | ISO 527-2 |
| Break | 2.2 | % | ASTM D638 |
| Break | 2.1 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 6890 | MPa | ASTM D790 |
| -- | 7750 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 159 | MPa | ASTM D790 |
| -- | 184 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 270 | J/m | ASTM D256 |
| 23°C 2 | 25 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 850 | J/m | ASTM D4812 |
| 23°C 3 | 53 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 7.00 | J | ASTM D3763 |
| -- | 13.1 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 161 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 4 | 163 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 156 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 5 | 159 | °C | ISO 75-2/Af |
| CLTE | ISO 11359-2 | ||
| Flow : -40 to 40°C | 4.5E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 9.3E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 232 to 243 | °C | |
| Middle Temperature | 243 to 254 | °C | |
| Front Temperature | 249 to 260 | °C | |
| Processing (Melt) Temp | 221 to 249 | °C | |
| Mold Temperature | 37.8 to 65.6 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Thermoplastic Polyolefin FT7013-721UV | RheTech, Inc. | Polyolefin, Unspecified | RheTech Thermoplastic Polyolefin |
| TAROPRENE® 1 A25 E1N | Taro Plast S.p.A. | TPV | TAROPRENE® |
| Exelene® PS 6800 | Montachem International, Inc. | PS (GPPS) | Exelene® PS |
| POLIFAIN 6020 | Fainplast Compounds S.r.l | PVC, Unspecified | POLIFAIN |
| TECACOMP® PA66 CF40 black 3623 | Ensinger GmbH | Nylon 66 | TECACOMP® |