Fiberfil® J-69/10/E
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Fiberfil® Engineered Plastics Inc. |
| Trademark: | Fiberfil® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | aqHEt3_Fiberfil-J-69-10-E.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Fiberfil®J-69/10/E is a polypropylene homopolymer (PP Homopoly) material, and the filler is 10% glass fiber reinforced material. This product is available in North America,. Fiberfil®The main features of J-69/10/E are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.978 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 9.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | ASTM D955 | ||
| 3.18 mm | 0.60 | % | ASTM D955 |
| 6.35 mm | 0.60 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.030 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 105 - 110 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 4140 | MPa | ASTM D638 |
| Tensile Strength (23°C) | 62.1 | MPa | ASTM D638 |
| Tensile Elongation (Yield, 23°C) | 3.5 | % | ASTM D638 |
| Flexural Modulus - Tangent (23°C) | 3100 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 79.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 48 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 154 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 143 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 204 - 221 | °C | |
| Middle Temperature | 216 - 232 | °C | |
| Front Temperature | 204 - 227 | °C | |
| Nozzle Temperature | 204 - 221 | °C | |
| Processing (Melt) Temp | 210 - 232 | °C | |
| Mold Temperature | 37.8 - 65.6 | °C | |
| Injection Rate | Slow | ||
| Back Pressure | 0.172 - 0.345 | MPa |
| Injection instructions |
|---|
| Screw speed: Slow to Medium |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® LLDPE 118N | Saudi Basic Industries Corporation (SABIC) | LLDPE | SABIC® LLDPE |
| Gallonprene® GP520-8505 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| HIVOREX 2600J | Lotte Chemical Corporation | HDPE | HIVOREX |
| LNP™ LUBRICOMP™ DCL32 compound | SABIC Innovative Plastics Europe | PC | LNP™ LUBRICOMP™ |
| Sylvin 83039-74 Brown 7462 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |